1. Giant Magneto Impedance Effect of Co-Based Metallic Fiber Under Bias Magnetic Field
The giant magneto impedance, GMI, effect of Co-based metallic fibers prepared by melt-extracted technology is investigated under different bias direct electrical current Ib. The GMI curves have single peaks which are symmetric about zero field at and below 1MHz. However, the bimodal GMI curves which have asymmetric peaks are observed when Ib is over 2mA at 0
Mat. Res.. Publicado em: 16/09/2019
-
2. Diameter Dependence of Magnetic Properties of Co-based Metal Fibers
Naked Co68.25Fe4.5Si12.25B15 metal fibers with diameter from 25 µm to 100 µm are produced by melt extraction method. Significant diameter dependence of magnetic properties is studied. Their microstructure and magnetic properties of hysteresis loops and giant magneto impedance (GMI) effect at frequencies from 0.1MHz to13MHz are investigated. The results sho
Mat. Res.. Publicado em: 09/09/2019
-
3. Structural, Morphological and Magnetic Properties of FeCo-(Fe,Co)3O4 Nanocomposite Synthesized by Proteic Sol-Gel Method Using a Rotary Oven
FeCo nanoparticles coated with (Fe,Co)3O4 (magnetite doped with cobalt) were synthesized by the proteic sol-gel chemical route. The synthesized materials were characterized by Thermogravimetry (TG), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), vibrating-sample magnetometer (VSM) and Mössbauer spectrosc
Mat. Res.. Publicado em: 18/03/2019
-
4. Facile Synthesis Strategy to Create Mesoporous Magnetic Iron Oxides Using Pectin-Based Precursors
Magnetic iron oxides are of great scientific and technological relevance. Therefore, herein, we report the research on developing methodologies for their sustainable and reproducible preparation. We discuss the synthesis of iron oxides involving citrus pectin as a source of energy (42 MJ kg-1) to promote the formation of the magnetic phases. The method invol
J. Braz. Chem. Soc.. Publicado em: 2017-07
-
5. Investigation of Structural, Morphological, Magnetic Properties and Biomedical applications of Cu2+ Substituted Uncoated Cobalt Ferrite Nanoparticles
ABSTRACT In the present work, Cu2+ substituted cobalt ferrite (Co1-xCuxFe2O4, x = 0, 0.3, 0.5, 0.7 and 1) magnetic nanopowders were synthesized via chemical co-precipitation method. The prepared powders were investigated by various characterization methods such as X-ray diffraction analysis (XRD), scanning electron microscope analysis (SEM), vibrating sample
Braz. arch. biol. technol.. Publicado em: 23/01/2017
-
6. The Effects of High Magnetic Field Annealing on the Structural Relaxation of Fe71(Nb0.8Zr0.2)6B23 Bulk Metallic Glass
Fe-based magnetic metallic amorphous and nanocomposites have excellent soft magnetic properties including greater magnetization and magnetic permeability compared with crystalline alloys, especially at high operation frequency and temperature. The high magnetic field (HMF) up to 12T is introduced to the heat annealing of Fe71(Nb0.8Zr0.2)6B23 bulk metallic gl
Mat. Res.. Publicado em: 04/12/2015
-
7. Study on Magnetic Behavior of Nd8Fe84Ti2B6 Nanocomposite by FORC Diagram
Systematic investigation was made on the magnetic property of a series of Nd2Fe14B/α-Fe nanocomposites prepared by crystallization of amorphous Nd8Fe84Ti2B6 ribbon at annealing temperatures in the range of 800-860 °C. Both remanence and energy product increase with increasing annealing temperature, reaching the maximum values at 850 °C. Coercivity remains
Mat. Res.. Publicado em: 04/12/2015
-
8. Structural and Magnetic Properties of Hydrothermal Spinel Ni0.4Zn0.6Fe2O4 Ferrites
Spinel ferrite powder with a nominal composition Ni0.4Zn0.6Fe2O4 was prepared by a hydrothermal method, following by sintering at 700 °C and 900 °C, respectively. The structural and magnetic properties of specimens are studied. It is found that the large particles in specimens are the agglomerates of many small nanoscale crystallites. A strengthening of ch
Mat. Res.. Publicado em: 17/11/2015
-
9. Syntheses and Fundamental Properties of Fe-rich Metastable Phase Alloys with Saturation Magnetization Exceeding 1.9 T
A melt-spun Fe90Si5B5 alloy ribbon consists of bcc-Fe(Si) + Fe3B + amorphous phase and exhibits good bending ductility, high tensile fracture strength above 1000 MPa, high corrosion resistance and unique magnetic properties as exemplified for high saturation magnetization exceeding 1.9 T, moderately high initial permeability of about 150 and low coercivity o
Mat. Res.. Publicado em: 23/10/2015
-
10. Influencia de la porosidad en las propiedades magnéticas de arreglos de nanohilos de Ni
ABSTRACTThe hysteresis properties of ordered arrays of Ni nanowires, electrodeposited into cylindrical nanoporous alumina membranes were investigated. The effect of the nanowire geometry (diameter and length), the array order and the nanowires' volume fraction on the array coercivity and remanence were analyzed. Porous alumina membranes were produced by a tw
Matéria (Rio J.). Publicado em: 2015-09
-
11. Facile preparation of Mn-doped CeO2 Submicrorods by composite-hydroxide-salt-mediated approach and their magnetic property
Mn-CeO2 submicrorods have been obtained from anomalous CeO2 particles though a novel composite-hydroxide-salt-mediated (CHSM) approach. This method is based on a reaction between a metallic salt and a metallic oxide in a solution of composite-hydroxide-salt eutectic at ~225 ºC and normal atmosphere without using an organic dispersant or capping agent. The m
Mat. Res.. Publicado em: 22/03/2013
-
12. Crescimento, estrutura e magnetismo de filmes ultrafinos de Ni depositados sobre Pd(100)
In this work, the growth mode, the structure and the magnetic behavior of ultrathin Ni films epitaxially grown over Pd(100) were investigated using in-situ experimental techniques ass RHEED, LEED, AES, MBE and MOKE, and ex-situ VSM. The objective was to study the influence of the stress induced by the lattice parameter mismatch of the materials (10,4%), the
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 27/02/2012