Study on Magnetic Behavior of Nd8Fe84Ti2B6 Nanocomposite by FORC Diagram
AUTOR(ES)
Jin, Jinling, Liu, Yuchao, Li, Kuoshe, Luo, Yang, Yu, Dunbo, Lu, Shuo, Xie, Jiajun, Lv, Binbin
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
04/12/2015
RESUMO
Systematic investigation was made on the magnetic property of a series of Nd2Fe14B/α-Fe nanocomposites prepared by crystallization of amorphous Nd8Fe84Ti2B6 ribbon at annealing temperatures in the range of 800-860 °C. Both remanence and energy product increase with increasing annealing temperature, reaching the maximum values at 850 °C. Coercivity remains around 5.5 kOe for the annealing temperatures above 800 °C. Although the smooth demagnetization curve indicates effective exchange coupling between the Nd2Fe14B/α-Fe dual phases, FORC diagram reveals the existence of α-Fe for the Nd8Fe84Ti2B6 ribbon annealed at 850 °C. In addition, the variation of microcoercivity at different locations indicates a distributed exchange interaction, which can be caused by the nonuniform microstructure. The magnetic property is also affected by the demagnetization effect caused by the particle shape, which is evidenced by the negative region in the first-order reversal curve (FORC) diagram.
Documentos Relacionados
- Study of Nd3+, Pd2+, Pt4+, and Fe3+ dopant effect on photoreactivity of TiO2 nanoparticles
- The Effects of High Magnetic Field Annealing on the Structural Relaxation of Fe71(Nb0.8Zr0.2)6B23 Bulk Metallic Glass
- Mudanças estruturais nas ligas Fe-(Nd,MM)-B e Fe77Nd15B8 submetidas a moagem de alta energia (MM=Mischmetal Brasileiro)
- Tartrazine degradation by supported TiO2on magnetic particles
- Assessment of the Fatigue Behavior of Ti-6Al-4V ELI Alloy with Surface Treated by Nd:YAG Laser Irradiation