Structural and Magnetic Properties of Hydrothermal Spinel Ni0.4Zn0.6Fe2O4 Ferrites
AUTOR(ES)
Zhang, Yiwei, Xia, Ailin, Chen, Weihua, Ma, Renjun
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
17/11/2015
RESUMO
Spinel ferrite powder with a nominal composition Ni0.4Zn0.6Fe2O4 was prepared by a hydrothermal method, following by sintering at 700 °C and 900 °C, respectively. The structural and magnetic properties of specimens are studied. It is found that the large particles in specimens are the agglomerates of many small nanoscale crystallites. A strengthening of chemical polarization of the internal chemical bonds is found in the powder specimen after sintering. The saturation magnetization increases from 50.1 emu/g for as-synthesized powder to 63.1 emu/g for specimen sintered at 900 °C mainly due to the weakening of spin canting, while the coercivity exhibits a slight decreasing variation with the increase of sintering temperature.
Documentos Relacionados
- Perovskite-Type Oxides La0.6M0.4Ni0.6Cu0.4O3 (M = Ag, Ba, Ce) towards the Oxygen Reduction Reaction (ORR) in Alkaline Medium: Structural Aspects and Electrocatalytic Activity
- Síntese de Fischer-Tropsch sobre perovskitas LayCu0,4Fe0,6O3
- Influence of the sintering temperature on the magnetic and electric properties of NiFe2O4 ferrites
- Facile synthesis of inverse spinel NiFe2O4 nanocrystals and their superparamagnetic properties
- Effect of fluorination treatment on electrochemical properties of M1Ni3.5Co0.6Mn0.4Al0.5 hydrogen storage alloy