Magnetic Hysteresis
Mostrando 1-12 de 59 artigos, teses e dissertações.
-
1. Cation Vacancies in NiFe2O4 During Heat Treatments at High Temperatures: Structural, Morphological and Magnetic Characterization
Nickel ferrite (NiFe2O4) was synthesized by mixing stoichiometric amounts of α-Fe2O3 and NiO using mechanical milling and heat treatments at high temperatures. The physical characterization of the samples was carried out using X-ray diffraction, infrared and Raman spectroscopies, Mössbauer spectrometry, magnetization measurements, scanning electron microsc
Mat. Res.. Publicado em: 20/12/2019
-
2. Comparison and Combination of Techniques for Determining the Parameters of a Magnetic Hysteresis Model
Abstract The Jiles-Atherton scalar hysteresis model presents five parameters used to represent the material tested and used to calculate the magnetic losses. This article presents a comparative analysis of the performance of two methods of identifying these parameters. In the first method, the equations of Jiles-Atherton were assembled into a single non-line
J. Microw. Optoelectron. Electromagn. Appl.. Publicado em: 12/09/2019
-
3. Diameter Dependence of Magnetic Properties of Co-based Metal Fibers
Naked Co68.25Fe4.5Si12.25B15 metal fibers with diameter from 25 µm to 100 µm are produced by melt extraction method. Significant diameter dependence of magnetic properties is studied. Their microstructure and magnetic properties of hysteresis loops and giant magneto impedance (GMI) effect at frequencies from 0.1MHz to13MHz are investigated. The results sho
Mat. Res.. Publicado em: 09/09/2019
-
4. Magnetic Aging, Anomalous and Hysteresis Losses
In this study the magnetic aging effect on anomalous and hysteresis loss was investigated, as well as its effect on domain morphology. For this purpose, non-oriented fully processed electrical steel with 2.3 wt.%Si - 79 ppm C and non-oriented semi-processed electrical steel annealed at 750 °C for 5 hours with 0.4 wt.%Si - 340 ppm C were aged at 150 °C. The
Mat. Res.. Publicado em: 21/03/2019
-
5. Thermal Behavior of Pyrite in the CO2 and N2 Atmosphere for Obtaining Pyrrhotite: A Magnetic Material
In the southern of Brazil the coal is composed of a large amount of pyrite (FeS2), an environmental problem for this region because the pyrite turns a waste. This work investigated the behavior of pyrite in CO2 and N2 atmospheres, aiming to identify better thermal treatment conditions of the pyrite waste that favor obtaining a material with magnetic properti
Mat. Res.. Publicado em: 18/10/2018
-
6. An Improved Method for Acquisition of the Parameters of Jiles-Atherton Hysteresis Scalar Model Using Integral Calculus
Abstract An accurate modeling of materials is essential to obtain reliable results in fields calculation. The Jiles-Atherton approach is widely used for modeling the magnetic hysteresis and depends on its set of five parameters to properly represent material. In this article is proposed an original methodology for obtaining this set of parameters avoiding th
J. Microw. Optoelectron. Electromagn. Appl.. Publicado em: 2017-03
-
7. Preparation and Properties of Epoxy Resin-Coated Micro-Sized Ferrosilicon Powder
Ferrosilicon powder surface coated with a dense epoxy resin membrane was prepared via coating precipitation methods using silane coupling agents as the modifier and epoxy resin as the coating agent. FTIR, FESEM, MPMS-XL, and TG-DSC were used to analyze the morphology, surface composition, magnetic property and thermostability of ferrosilicon powder before an
Mat. Res.. Publicado em: 07/07/2016
-
8. Magnetic and Electrical Properties of MnxCu1-xFe2O4 Ferrite
In the present work, mixed manganese-copper ferrite of composition MnxCu1-xFe2O4 (within x=0.40, 0.42, 0.44, 0.46, 0.48 and 0.50) have been investigated for their electric and magnetic properties such as dc resistivity, Curie temperature, saturation magnetization. MnxCu1-xFe2O4 ferrite samples were prepared by uniaxial pressing from the oxide mixture, synthe
Mat. Res.. Publicado em: 31/05/2016
-
9. The Effects of High Magnetic Field Annealing on the Structural Relaxation of Fe71(Nb0.8Zr0.2)6B23 Bulk Metallic Glass
Fe-based magnetic metallic amorphous and nanocomposites have excellent soft magnetic properties including greater magnetization and magnetic permeability compared with crystalline alloys, especially at high operation frequency and temperature. The high magnetic field (HMF) up to 12T is introduced to the heat annealing of Fe71(Nb0.8Zr0.2)6B23 bulk metallic gl
Mat. Res.. Publicado em: 04/12/2015
-
10. Influence of Milling Time During the Mechanical Alloying Process on the Properties of Fe-3Si-0.75P Alloy
AbstractIn this study the soft magnetic alloy Fe-3Si-0.75P (wt%) was obtained by mechanical alloying through powder metallurgy. The processing included the formulation of metallic powder, wet milling for 1 h, 3 h, 6h and 9 h, in an attritor mill using alcohol P.A. as a lubricant. Cold compaction was then performed in a floating die under 600 MPa pressure and
Mat. Res.. Publicado em: 2015-10
-
11. Influencia de la porosidad en las propiedades magnéticas de arreglos de nanohilos de Ni
ABSTRACTThe hysteresis properties of ordered arrays of Ni nanowires, electrodeposited into cylindrical nanoporous alumina membranes were investigated. The effect of the nanowire geometry (diameter and length), the array order and the nanowires' volume fraction on the array coercivity and remanence were analyzed. Porous alumina membranes were produced by a tw
Matéria (Rio J.). Publicado em: 2015-09
-
12. Synthesis and characterization of Fe3O4 nanoparticles with perspectives in biomedical applications
Nowadays the use of magnetic nanoparticles (MNP) in medical applications has exceeded expectations. In molecular imaging, MNP based on iron oxide coated with appropriated materials have several applications in vitro and in vivo studies. For applications in nanobiotechnology these MNP must present some characteristics such as size smaller than 100 nanometers,
Mat. Res.. Publicado em: 29/04/2014