Influence of Milling Time During the Mechanical Alloying Process on the Properties of Fe-3Si-0.75P Alloy
AUTOR(ES)
Pelegrini, Leandro, Bittencourt, Sérgio Deitos, Pauletti, Philippe, Verney, José Carlos Krause de, Dias, Moisés de Mattos, Schaeffer, Lírio
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
2015-10
RESUMO
AbstractIn this study the soft magnetic alloy Fe-3Si-0.75P (wt%) was obtained by mechanical alloying through powder metallurgy. The processing included the formulation of metallic powder, wet milling for 1 h, 3 h, 6h and 9 h, in an attritor mill using alcohol P.A. as a lubricant. Cold compaction was then performed in a floating die under 600 MPa pressure and, finally the ring-shaped test specimens were sintered at 1150 °C for 1h. The electrical, physical and magnetic properties were then analyzed using the following assays: Laser granulometry, density, metallography, hysteresis curve and AC permeability, resistivity and XRD. The results showed a strong influence of milling time on magnetic properties of the alloy. There was a decrease in grain size with the milling time, which is likely the cause of increased in magnetic properties.
Documentos Relacionados
- The effects of mechanical alloying on the extrusion process of AA 6061 alloy reinforced with Si3N4
- Effect of heat treatment on Fe-B-Si-Nb alloy powder prepared by mechanical alloying
- Temperature and Deposition Time Effect on Properties and Kinetics of CdSe and CdS0.25Se0.75 Films Deposited by CBD
- Prediction of Mechanical Properties of AlSi13Cu2Fe Alloy Using the ATND Methods
- Effect of Extrusion and Heat Treatment on Microstructure and Mechanical Properties of Hypereutectic A390-0.3wt%Nd Alloy