Ceramic Material
Mostrando 1-12 de 357 artigos, teses e dissertações.
-
1. Bioactive SiO2-K2O-CaO-P2O5 glass-ceramic scaffold prepared using polyurethane foam template
Abstract A glass-ceramic in the SiO2-K2O-CaO-P2O5 quaternary system was prepared by substituting the Na2O component with K2O to avoid Na2Ca2Si3O9 formation upon thermal treatment since this phase decreases apatite formation kinetics on glass material. To form the glass-ceramic, a modified sol-gel method involving solution precipitation, followed by reagents
Cerâmica. Publicado em: 2023
-
2. A review on the ceramic additive manufacturing technologies and availability of equipment and materials
Abstract Ceramic additive manufacturing allows the fabrication of small series of complex parts without the high costs of molds usually associated with traditional ceramic processing. Although research into ceramic 3D printing by all technologies started back in the 90s, its industrial application is still quite restricted when compared to polymers and metal
Cerâmica. Publicado em: 2022
-
3. Analysis of Al2O3-ZrO2 ceramic insert in turning process of Ti-6Al-4V alloy using grey Taguchi-based response surface methodology (GT-RSM)
Abstract The present investigation aimed at a sustainable green turning operation of Ti-6Al-4V alloy using multi-objective optimization of surface roughness, tool flank wear, material removal rate, and tool wear loss with cutting speed, feed rate, and depth of cut as input parameters. The experiments were performed on a CNC lathe machine using an alumina-zir
Cerâmica. Publicado em: 2022
-
4. Evaluation of the self-healing capacity of ceramics produced with alumina and silicon carbide
Abstract The self-healing capacity of a ceramic material produced by uniaxial pressing with alumina (Al2O3), silicon carbide (SiC), and magnesium oxide (MgO) was evaluated. To assess self-healing, a discontinuity was generated on the surface of the specimens. The healing time in the oven, at a temperature of 1000 ºC, was 1, 30, and 60 min. The specimens wer
Cerâmica. Publicado em: 2022
-
5. Microstructural characteristics, properties, synthesis and applications of mullite: a review
Abstract Mullite, an intermediate phase of the binary alumina-silica system, is one of the most important phases of ceramic products containing alumina and silica in the initial composition. Its stoichiometry ranges from 3Al2O3.2SiO2 (3:2) to 2Al2O3.SiO2 (2:1) and its crystalline structure is orthorhombic, characterized by the presence of octahedral chains o
Cerâmica. Publicado em: 2022
-
6. Three-dimensional assessment of internal adaptation measurement of three cad/cam ceramic systems
Resumo Este estudo teve como objetivo avaliar a adaptação interna de três diferentes coroas cerâmicas CAD/CAM (Computer-aided design/computer-aided manufacturing). A adaptação interna de um material cerâmico de rede com infiltração de polímero (Vita Enamic [VE]) foi comparada com duas cerâmicas de vidro maquináveis; silicato de lítio reforçado
Brazilian Dental Journal. Publicado em: 2022
-
7. Evaluation of the use of silica-alumina refractory waste as a supplementary cementitious material
Abstract The use of supplementary cementitious materials (SMCs) is one of the three essential factors for the sustainability of the cement industry. To reduce CO2 emissions, several studies have introduced new methods for the utilization of industrial wastes such as the addition into cementitious materials. The objectives of this study were to chemically and
Cerâmica. Publicado em: 2021-06
-
8. Effects of sintering temperature on microstructure and properties of sanitaryware ceramic produced with waste material
Abstract This paper aims at exploring the possibility of using a great percentage of recycled materials into vitreous china (VC), thus, contributing to urban waste decrease while lowering the industry’s buying costs, previously optimized, for the sanitaryware production. The recycled blend was introduced in the ceramic slip, Sanitser VC, and used in three
Cerâmica. Publicado em: 2021-03
-
9. PROPRIEDADES DE PROTEÇÃO TÉRMICA DO CARBETO DE SILÍCIO EM REVESTIMENTOS CERÂMICOS
In recent years, research on the development of protective materials has expanded significantly in order to find efficient and economically viable solutions for application in various industrial segments. Among these materials, those aimed at protecting metallic substrates against high temperatures that end up causing corrosive processes, stand out due to th
Quím. Nova. Publicado em: 2021-01
-
10. PROCESSING OF A METAL CONCENTRATE FROM GROUND WASTE PRINTED CIRCUIT BOARDS IN ACIDIC MEDIA USING HYDROGEN PEROXIDE AS OXIDANT
The recovery of precious and base metals of a metal concentrate from ground waste printed circuit boards (PCBs) is described in detail. Samples were treated with NaOHaq. to remove the soldering mask. Experiments were performed in acidic medium (HF, H2SO4, CH3COOH or H3PO4) using H2O2 as oxidant. Base metals were leached in high yields (>99 wt.%) at ~40 ºC a
Quím. Nova. Publicado em: 20/07/2020
-
11. The Tatuí Formation as a source of raw material in the ceramic pole of Santa Gertrudes (SP)
Abstract The importance of the Santa Gertrudes Ceramic Complex (SGCC) in the ceramic market is directly associated with the high quality of the Corumbataí Formation clays used in the manufacture of its products. Although the volumetric capacity of the Corumbataí Formation is able to meet the SGCC demand for the coming years, its industries are always in se
REM, Int. Eng. J.. Publicado em: 2020-03
-
12. Color Stability of Ceramic Veneers Luted With Resin Cements and Pre-Heated Composites: 12 Months Follow-Up
Resumo O objetivo foi avaliar a estabilidade de cor de laminados cerâmicos de fina espessura, após a cimentação com cimentos resinosos e resinas compostas em temperatura ambiente e aquecida (60oC), durante 12 meses; bem como determinar o grau de conversão dos diferentes materiais para cimentação. Foram utilizados dois cimentos resinosos [AllCem Veneer
Braz. Dent. J.. Publicado em: 2020-01