Phosphorus emitter and metal - grid optimization for homogeneous (n+p) and double-diffused (n++n+p) emitter silicon solar cells

AUTOR(ES)

Sánchez, Manuel Cid, Stem, Nair

FONTE

Materials Research

DATA DE PUBLICAÇÃO

2009-03

RESUMO

This work focuses on studying two types of structure: homogeneous and double-diffused emitter silicon solar cells. The emitter collection efficiencies and the recombination current densities were studied for a wide range of surface dopant concentrations and thicknesses. The frontal metal-grid was optimized for each emitter, considering the dependence on the metal-semiconductor contact resistivity and on the emitter sheet resistance. The best efficiency for n+p structures, η≈ 25.5%, is found for emitters with thicknesses between (0.5-3) µm and surface doping concentrations in the range 2 x 10(19) cm-3- 4 x 10(18) cm-3; while the n++n+p structure a maximum efficiency of η≈ 26.0% was identified for an even wider range of emitter profiles.

Documentos Relacionados

• Studies of phosphorus Gaussian profile emitter silicon solar cells
• Homogeneous Gaussian Profile P+-Type Emitters: Updated Parameters and Metal-Grid Optimization
• Análise teórica de emissores homogêneos (n+) e duplamente difundidos (n+n++) em células solares de silício: implementações ao processo de fabricação.
• Analysis of thin bifacial silicon solar cells with locally diffused and selective back surface field
• Development and comparison of n+pn+ and n+pp+ solar cells in multicrystalline silicon