Estudo de camadas dielétricas para aplicação em capacitores MOS. / Study of dielectric layers for MOS capacitors.

AUTOR(ES)
DATA DE PUBLICAÇÃO

2007

RESUMO

Silicon oxynitride films obtained by the PECVD technique from N2O+SiH4+He gaseous mixtures, at 320°C, with different deposition pressure and RF power were studied intending to improve the interface quality with Si, decreasing the effective charge density and the interface state density in order to utilize them in MOS semiconductor devices. The results showed that with a deposition pressure of 0.160 mbar and a RF power density lower than 125 W/cm2 it is possible to obtain interface state density (Dit) values of 4x1010 eV-1.cm-2, Electrical Breakdown (Ebd) of 13 MV/cm, comparable with the obtained for thermally grown SiO2 , and an effective charge density (Nss) of 4x1011 cm-2. According with experimental results this Nss value is the minimum attainable with our chemical cleaning process. In this way it can be said that these results are very promising, considering that these materials were obtained by PECVD at low temperatures, but still viable for MOS devices application. In order to initiate studies with high dielectrics constant material, TiOx films (k= 40-180), obtained by reactive sputtering through the Ar+O2 gaseous mixture utilizing a Ti target, were chosen. MOS capacitors with these films were fabricated and dielectric constant values varying from 40 to 160 were obtained. However, until now, these materials have presented appreciable leakage current values, which were, minimize by orders of magnitude with the addition of a thin SiO2 or SiOxNy (optimized in this work) layer at the interface were utilized. This thin layer also resulted in a significant improvement of the interface quality. Utilizing double dielectric layer with SiOxNy or SiO2, still thick (³ 1nm) as intermediate layer a dielectric constant value of 20 was obtained. Its important to mention that the SiOxNy and TiOx films, and consequently the double layer, were deposited at low temperatures.

ASSUNTO(S)

silício capacitores dielétricos (propriedades) titanium oxide dispositivos semicondutores silicon oxynitride high k dielectrics low temperature mos capacitors estrutura dos materiais

ACESSO AO ARTIGO

Documentos Relacionados