25. Compósitos cerâmicos porosos de alumina - zircônia para aplicação em sistemas de controle térmico para satélites: obtenção e caracterização / Alumina-zirconia porous ceramic composites for application in satellite thermal control systems: obtaining and characterization
To control the temperature of satellites are used various thermal control heat systems. The Loop Heat pipe (LHP) are being developed at the DEM (Space Mechanic and Control Division) of the INPE (National Institute for Space Research) an apparatus for passive heat control of the satellites components. The main components of the LHP system are: capillary evapo
Publicado em: 2008
-
26. Sinterização e propriedades mecânicas do compósito Y-TZP/Al2O3
Foi estudado o efeito da adição de Al2O3 nas propriedades de cerâmicas à base de ZrO2 tetragonal estabilizada com ítria (Y-TZP) visando sua aplicação como material dentário. Amostras contendo 0, 10, 20 e 30% em peso de Al2O3 foram compactadas por prensagem uniaxial a frio (80 MPa) e em seguida sinterizadas ao ar a 1500, 1550 e 1600 °C por 120 min. O
Cerâmica. Publicado em: 2007-09
-
27. Fotoluminescência em ZrO2 dopado com Y e La
O objetivo deste trabalho é descrever a síntese e a caracterização óptica de uma solução sólida de óxido de zircônio contendo ítrio e lantânio. Foram misturados citrato de zircônio, nitrato de ítrio e nitrato de lantânio nas proporções 94 mol% ZrO2-6 mol% Y2O3 e 92 mol% ZrO2-6 mol % Y2O3-2 mol % La2O3. A análise de espectroscopia de absorç
Cerâmica. Publicado em: 2007-03
-
28. Determinação quantitativa de fases em ZrO2 (MgO) (Y2O3) utilizando o Método de Rietveld / QUANTITATIVE DETERMINATION OF PHASES IN ZRO2 (MGO) (Y2O3) USING THE RIETVELD METHOD
O objetivo principal deste trabalho é a caracterização cristalográfica da zircônia co-estabilizada com ítria e magnésia, aplicando o método de Rietveld aos dados de difração de raios X, para a análise quantitativa de fases dos polimorfos da zircônia (monoclínica, tetragonal e cúbica ). As amostras de zircônica foram obtidas com dopagem de óxi
Publicado em: 2007
-
29. STUDY OF THE FORMATION OF SECONDARY PHASES IN THE COMPOSITE LSM/YSZ / Estudo da formação de fases secundárias no compósito LSM/YSZ
O compósito de manganito de lantânio dopado com estrôncio (La1-xSrxMnO3 - LSM) e zircônia estabilizada com ítria (ZrO2/Y2O3 - YSZ), tem sido indicado como catodo das células a combustível de óxido sólido, por apresentar melhor desempenho como eletrodo catódico na região da tripla fase reacional (TRIPLE PHASE BOUNDARY - TPB), formada na interface e
Publicado em: 2007
-
30. Efeito da zircônia na sinterização de SiC com adições de Al2O3 e Y2O3
A sinterização em fase líquida de carbeto de silício (SiC) com adições de Al2O3, Y2O3 e ZrO2 foi estudada. O processo de moagem de alta energia resultou na aditivação secundaria do pó, sendo que a majoritária foi de ZrO2 [1]. As microestruturas obtidas tiveram sua fases cristalinas fortemente influenciadas pelo tamanho médio de partícula do pó,
Cerâmica. Publicado em: 2006-09
-
31. Influence of ion nitriding process on the properties of zirconia coating deposited on stainless steel
ZrO2-3 mol % Y2O3-coated AISI 310 stainless steel was nitrided using plasma produced by dc pulsed discharge in a mixture of N2 and H2 at an equilibrium temperature of 450ºC. Profile chemical analyses with GDOS (glow discharge optical spectroscopy) and XRD showed the formation of Nitrogen/Y-ZrO2 solid solution. Nitrogen atoms enter in the zirconia substituti
Brazilian Journal of Physics. Publicado em: 2006-09
-
32. "Eletrólitos sólidos cerâmicos à base de óxido de zircônio para a detecção de oxigênio" / "Zirconium oxide based ceramic solid electrolytes for oxygen detection"
Taking advantage of the high thermal shock resistance of zirconia-magnesia ceramics and the high oxide ion conductivity of zirconia-yttria ceramics, composites of these ceramics were prepared by mixing, pressing and sintering different relative concentrations of ZrO2: 8.6 mol% MgO and ZrO2: 3mol% Y2O3 solid electrolytes. Microstructural analysis of the compo
Publicado em: 2003
-
33. Zircônia tetragonal policristalina. Parte II: Microestrutura e resistividade elétrica
Nesta segunda parte são mostrados os resultados obtidos em cerâmicas densas de ZrO2: 3% mol Y2O3 (Y-TZP) e 12% mol CeO2 (Ce-TZP), analisadas por espectroscopia Raman, microscopia eletrônica de varredura, e por espectroscopia de impedância. Os resultados mostram que, para ambos tipos de amostras, é possível obter cerâmicas densas (> 95% da densidade te
Cerâmica. Publicado em: 2001-06
-
34. Comportamento óptico estrutural da zircônia dopada com Er3+,Pr3+ e estabilizante de fase Y3+ / Optical and structural behavior of the ZrO2 doped with Er3+, Pr3+ and Y3+
O objetivo deste trabalho é a produção e caracterização de filmes finos de Zircônia (ZrO2) dopada com íons terras raras Er3+, Pr3+ estabilizante de fase y3+. Os filmes foram produzidos por evaporação térmica através de canhão de elétrons (EB-PVD) em um sistema não comercial de evaporação desenvolvido em nosso laboratório, onde conseguimos pr
Publicado em: 1999
-
35. Sintering and Thermal Ageing Studies of Zirconia - Yttria Ceramics by Impedance Spectroscopy / Estudos de Sinterização e de Envelhecimento Térmico de Cerâmicas de Zircônia - Ítria por Espectroscopia de Impedância
Eletrólitos sólidos cerâmicos de ZrO2:8% mol Y2O3 foram preparados com pós de três origens: pó comercial fabricado pela Nissan (Japão), pó obtido por coprecipitação dos hidróxidos no IPEN e pó obtido por mistura de óxidos (utilizando-se ZrO2 produzido na Usina de Zircônio do IPEN e Y2O3 (USA) de pureza superior a 99,9%). Esses materiais de part
Publicado em: 1998
-
36. Enhanced oxygen diffusivity in interfaces of nanocrystalline ZrO2⋅Y2O3
First measurements of oxygen grain boundary diffusion coefficients in nanocrystalline yttria-doped ZrO2 (n-ZrO2⋅6.9 mol % Y2O3) are presented. The 18O diffusion profiles measured by secondary ion mass spectroscopy are much deeper in the nanocrystalline specimens than in single crystals. An oxygen diffusivity, DB, in the grain boundaries can be deduced, whi