Mostrando 13-24 de 36 artigos, teses e dissertações.
-
13. Influence of starch type on characteristics of porous 3Y-ZrO2 prepared from a direct consolidation casting method
Starch consolidation casting has been successfully used to produce porous ceramics with complex shapes at a relatively low producing cost. In this work, porous 3Y-ZrO2 ceramics were produced using two types of starch (corn and potato). Concentrated (50-52 vol. (%)) aqueous suspensions of the different 3Y-ZrO2-starch mixtures (i.e. starch to zirconia weight r
Materials Research. Publicado em: 01/04/2011
-
14. Thermal barrier coating by electron beam-physical vapor deposition of zirconia co-doped with yttria and niobia
Abstract: The most usual ceramic material for coating turbine blades is yttria doped zirconia. Addition of niobia, as a co-dopant in the Y2O3-ZrO2 system, can reduce the thermal conductivity and improve mechanical properties of the coating. The purpose of this work was to evaluate the influence of the addition of niobia on the microstructure and thermal prop
J. Aerosp. Technol. Manag.. Publicado em: 2010-08
-
15. Cerâmicas dentárias à base de ZrO2, aditivadas com biovidro: processamento, caracterização estrutural e mecânica / Dental ceramics to the base of ZrO2 enriched with bioglass: Processing, Structural and Mechanics Characterization
Neste trabalho, foi desenvolvida e caracterizada a cerâmica à base de zircônia tetragonal aditivada com biovidro para aplicações em implantes ou próteses. Essa zircônia (Y-TZP) tem conteúdo de 3% em mol de Y2O3, com objetivo de estabilizar a fase metaestável tetragonal, a qual possui características de conferir características tenacificantes ao ma
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 06/11/2009
-
16. Characterization mechanical of ZrO2 (3%Y2O3) ceramics nanostructured and e microstructured / Caracterização mecânica de cerâmicas à base de ZrO2 (3%Y2O3) nano e microparticuladas
In this work, dental commercial ceramics the base of ZrO2 stabilized with yttrium had been sintering and characterized how much to its physical and mechanical properties. The nanostructuralized commercial blocks (ProtMat) had been sintering in different temperatures, 13000C and 14000C, and the microstructuralized ones (IVOCLAR and ZIRCONZHAN and ProtMat) had
Publicado em: 2009
-
17. Synthesis and sintering of ZrO2 - 4,5%Y2O3 nanoparticles / Obtenção e sinterização de nanopartículas de ZrO2-4,5%Y2O3
The powders synthesis of yttria-stabilized zirconia by chemical methods has enabled the reduction in particle size for the submicrometer-sized scale. This reduction is to improve the electrical and mechanical responses of electrolyte fuel cells. Contributing in this research, this work was to study the effects of temperature elimination of organic phases, to
Publicado em: 2009
-
18. Caracterizações estruturais e espectroscópicas de cerâmicas ferroelétricas de PLZT dopadas com íons de terras raras trivalentes / Structural and spectroscopy characterization of rare-earth doped PLZT ferroelectric ceramics
Recentemente, grande interesse tem sido demonstrado por cerâmicas transparentes dopadas com íons terras raras trivalentes, como meios ativos para lasers na região espectral do infravermelho próximo. Em particular, cerâmicas dopadas com altas concentrações de Nd3+ e Yb3+ são muito estudadas pela possibilidade de gerar emissão laser de alta potência
Publicado em: 2009
-
19. Condutividade elétrica da solução sólida céria-zircônia dopada com ítrio e gadolínio / Electrical conductivity of solid solution ceria-zirconia doped yttria and gadolinium
Rare earth doped ceria has a great potential to be used as electrolyte in temperatures around 800 C in fuel cells due to its higher electrical conductivity than YSZ. However, the reduction of Ce+4 to Ce+3 in low oxygen partial pressure has introduced limitations for using doped ceria electrolyte due to electronic conduction. Among the several ceria solid sol
Publicado em: 2009
-
20. Obtenção e caracterização de perovskitas supercondutoras monocristalinas do tipo YxPr1-xBa2Cu3O7-δ dopadas por Fe, Ni, Ga e Zn
O Praseodímio é conhecido por ter um comportamento singular na família dos cupratos supercondutores de alta temperatura crítica do tipo RE-123. Quando esses cupratos são dopados com Praseodímio a temperatura crítica aparentemente diminui, ocorrendo uma transição metal-isolante. A origem deste comportamento, sendo de interesse fundamental, pode forne
Publicado em: 2009
-
21. Propriedades elétricas e microestrutura de Céria dopada com Gd+3 e Y+3 para aplicação como eletrólitos em pilhas a combustível
Fonte de Energia Alternativa, Renovável e Limpa é um tema cada vez mais presente no dia a dia da atual sociedade mundial. Pilhas a combustível surgem como uma opção real para tornar as fontes alternativas um dos principais modos de geração de energia em futuro próximo. Zircônia estabilizada com 8% mol de ítria (ZEI8) é o material mais utilizado co
Matéria (Rio de Janeiro). Publicado em: 2008-09
-
22. Propriedades reológicas e microestruturais de eletrólito de ZrO2/Y2O3
Para reduzir a temperatura de operação das pilhas a combustível de óxido sólido (PaCOS), estruturas com filmes finos de eletrólito depositados, por aerografia, sobre suportes de anodo porosos foram desenvolvidas. As barbotinas, empregadas para fabricação dos filmes, foram preparadas a partir de suspensões com pós de zircônia estabilizada com ítri
Matéria (Rio de Janeiro). Publicado em: 2008-09
-
23. Performance of 3Y-TZP bioceramics under cyclic fatigue loading
In this work, the static mechanical properties and cyclic fatigue life of 3 mol. (%) Y2O3-stabilized tetragonal zirconia polycrystalline (3Y-TZP) ceramics were investigated. Pre-sintered samples were sintered in air at 1600 °C for 120 minutes, and characterized by X ray diffraction and scanning electronic microscopy. Hardness and fracture toughness were det
Materials Research. Publicado em: 2008-03
-
24. Study of nickel catalysts supported on modified ZrO2 applied in reforming reactions / Estudo de catalisadores de níquel suportados em ZrO2 modificados aplicados em reações de reforma
Zirconium dioxide is a material with physics and chemical characteristics that can be applied in many fields, as academic as industrial. In the catalysis, the interest in systems based on zirconia (ZrO2) are growing- up quickly, as a catalyst as a support, considering that ZrO2 properties can be changed by the addition of different cations. The objective of
Publicado em: 2008