Yba2cu3o7 8
Mostrando 1-7 de 7 artigos, teses e dissertações.
-
1. Chemical Stability and Crystallographic Analysis of the the Sr2HoNbO6 Cubic Perovskite as Potential Substrate for YBa2Cu3O7-δ Superconducting Films
The Sr2HoNbO6 complex perovskite has been synthesized by solid-state reaction. X-ray diffraction pattern reveals that Sr2HoNbO6 material crystallizes in a cubic structure, Fm3̅m space group, lattice constant a=8.018 Å, which has a lattice mismatch ~3% with YBa2Cu3O7-δ. The chemical stability of Sr2HoNbO6 with YBa2Cu3O7-δ superconducting has been studied
Mat. Res.. Publicado em: 07/07/2016
-
2. Unsynchronized resonance of covalent bonds in the superconducting state
Cálculos DFT em modelos de cluster de cupratos (LaBa2Cu3O6.7, La1.85Sr0.15CuO4, YBa2Cu3O7, TlBa2Ca2Cu3O8.78, HgBa2Ca2Cu3O8.27), de sistemas metálicos (Nb3Ge, MgB2) e do pnictido LaO0.92F0.08FeAs indicaram a ocorrência da ressonância não-sincronizada no estado supercondutor, como prevê a teoria RVB (resonating valence bond) de Pauling. Para os cupratos,
Journal of the Brazilian Chemical Society. Publicado em: 2012-07
-
3. Efeitos de pressão nas flutuações termodinâmicas da condutividade elétrica de supercondutores de alta temperatura crítica
O presente trabalho consiste de um estudo experimental dos efeitos de pressão externa sobre as flutuações termodinâmicas da condutividade elétrica de supercondutores de alta temperatura crítica (HTSC). Para tanto, medidas de resistividade elétrica em função da temperatura foram realizadas em condições de pressão hidrostática aplicada até valore
Publicado em: 2007
-
4. Efeitos de ordenamento chiral em supercondutores e sistemas magnéticos desordenados
Este trabalho apresenta uma investigação experimental sobre as propriedades magnéticas e de transporte elétrico de sistemas caracterizados por desordem e frustração. Tais sistemas são amostras granulares do supercondutor de alta temperatura crítica YBa2Cu3O7-δ e amostras do tipo vidro-de-spin e reentrantes das ligas magnéticas diluídas AuMn 8at% e
Publicado em: 2007
-
5. High-temperature superconductivity
The widely held notion that high-temperature superconductivity originates in the cuprate-planes is proven to be faulty. In the cuprates such as YBa2Cu3O7, we argue that the superconductivity resides in the BaO layers. This superconductivity is s-wave, not d-wave, in the bulk. The trio of ruthenate compounds, doped Sr2YRuO6, GdSr2Cu2RuO8, and Gd2-zCe zSr2Cu2R
Brazilian Journal of Physics. Publicado em: 2003-12
-
6. Single cristal growth of YBa2Cu3O7-ä superconductor the flux method using SnO2 crucibles. / Crescimento de monocristais supercondutores de YBa2Cu3O7-ä pelo método de fluxo em cadinhos de SnO2.
O método do fluxo tem se tornado uma das técnicas mais usadas, quando se trata de crescimento de monocristais supercondutores de YBa2Cu3O7-ä. A técnica processa o material no estado fundido e isto acarreta temperaturas nas quais reações podem acontecer. Na preparação de monocristais supercondutores da família Y-Ba-Cu-O, mais especificamente, YBa2Cu3
Publicado em: 1998
-
7. Efeitos da substituição do Cu por Mn no composto YBA2Cu3O7-G
Samples of the compounds YBa2(Cu1-xMnx)3O7-d , x = 0,0, 0,01, 0,025, 0,05, 0,075, 0,10, 0,15 e 0,20, were sintered at. 950º, 970º e 1020º C. These samples were characterized by X ? ray diffraction, optical metallography, electrical resistivity and magnetic susceptibility. Superconductivity around 92 K for all samples. The YBa2Cu3O7-d solubility limit for
Publicado em: 1990