Efeitos da substituição do Cu por Mn no composto YBA2Cu3O7-G
AUTOR(ES)
Renato de Figueiredo Jardim
DATA DE PUBLICAÇÃO
1990
RESUMO
Samples of the compounds YBa2(Cu1-xMnx)3O7-d , x = 0,0, 0,01, 0,025, 0,05, 0,075, 0,10, 0,15 e 0,20, were sintered at. 950º, 970º e 1020º C. These samples were characterized by X ? ray diffraction, optical metallography, electrical resistivity and magnetic susceptibility. Superconductivity around 92 K for all samples. The YBa2Cu3O7-d solubility limit for Mn is very small, less than x = 0,005. This fact means precipitation of non-superconducting additional phases, whose stoichiometric were identified as Y2BaCuO5 and Ba3Mn2O8. The presence of this phases changes substancially the microstructure of the samples. This effect being greater for the samples sintered at 970º C. For this series of samples it was observed na anomaly in the thermal transport properties induced by the microstructural modifications
ASSUNTO(S)
magnesio compostos de cobre supercondutores
ACESSO AO ARTIGO
http://libdigi.unicamp.br/document/?code=vtls000036645Documentos Relacionados
- Efeitos das substituições químicas na irreversibilidade magnética e magnetocondutividade do supercondutor YBa2 Cu3 O7-[delta]
- Depinning do fluxo de Josephson em compósitos YBa 2 Cu 3 O 7-delta/Ag
- Estudo das propriedades magnéticas e resistivas do YBa2Cu3O7−d supercondutor
- Structural and magnetic properties of YBa2Cu3O7/BaZrO3 composites
- PROCESSAMENTO E CARACTERIZAÇÃO DE COMPÓSITOS SUPERCONDUTORES YBa2Cu3O7-d/ Ag