1. Metal-Supported Niobium Catalysts Investigation for Conversion of Bio-Renewable Glycerol to Organic Compounds
The glycerol oxidative dehydration to organic compounds, especially acrolein and acrylic acid, was studied over vanadium, molybdenum, and cobalt oxides supported on niobium oxide and niobium phosphate catalysts. At 300 °C, the glycerol conversion was 100% over all catalysts tested, and acrolein was the main product observed, without significant deactivation
Journal of the Brazilian Chemical Society. Publicado em: 2022
-
2. Monochromatic double coloring effect on V2O5 thin films deposited by electron beam
ABSTRACT Electrochromic material is a thin film technology that has a close relationship with environmental sustainability since they can control the light and heat that enter and leave a building. Vanadium oxide films are electrochemically active for lithium and electron co-intercalation, presenting low optical variation in the low energy visible light, whi
Matéria (Rio J.). Publicado em: 25/11/2019
-
3. Oxidative Dehydration of Glycerol over Molybdenum- and Vanadium-Based Catalysts
Surplus of glycerol production from the biodiesel industry has led to the search for glycerol conversion routes, the most common of which are dehydration and oxidative dehydration. Vanadium and molybdenum oxides were supported on γ-Al2O3 and their properties were analyzed through several characterization techniques, showing that the acidity increases after
J. Braz. Chem. Soc.. Publicado em: 08/04/2019
-
4. Commitment Between Roughness and Crystallite Size in the Vanadium Oxide Thin Film opto-electrochemical Properties
The V2O5 thin films has been widely studied because it has application as ionic host in electrochromic and lithium-ion batteries, two technologies that have an intimate connection with sustainability as substitutes for fossil energies and as agents for improving energy efficiency. In electrochromic technology, V2O5 is applied as a passive electrode due to it
Mat. Res.. Publicado em: 01/11/2018
-
5. Efecto de la sustitución de V por Ti sobre las temperaturas de transformación de fase y el desajuste de red matriz/precipitado en la superaleación 76Fe-12Al-12V
ABSTRACT Fe-Al based alloys have a remarkable potential for high temperature structural applications, provided that the limitation of their low creep resistance is solved. Third element addition (Nb, Ti, Zr or Ta) has proven to per-form the task, at the expense of a low ductility. In previous works we have investigated ferritic alloys in the Fe-Al-V system w
Matéria (Rio J.). Publicado em: 19/07/2018
-
6. CORRELAÇÕES GEOQUÍMICAS ENTRE AMOSTRAS DE PETRÓLEO DA BACIA POTIGUAR E DEFINIÇÃO DE SUAS POSSÍVEIS ROCHAS GERADORAS
Eight petroleum samples from Potiguar Basin were submitted for determination of saturated biomarkers by gas chromatography (fingerprint), liquid chromatography (saturates, aromatics, resins and asphaltenes), gas chromatography-mass spectrometry (GC-MS), nickel and vanadium by high resolution continuum source graphite furnace atomic absorption spectrometry (H
Quím. Nova. Publicado em: 2018-04
-
7. Electroremediation of deactivated catalysts from fluidised catalytic cracking for vanadium removal - the effect of a dual cathode chamber reactor
Abstract The aim of this study was to evaluate the quantity of vanadium removed through electrokinetic remediation applied to catalyst waste used in a fluid catalytic cracking process. In excess, vanadium affects process efficiency by reducing the catalyst’s activity, causing deactivation and reducing its useful life in petroleum cracking during refining.
Braz. J. Chem. Eng.. Publicado em: 2018-01
-
8. Efecto del V y el Si Sobre la Microestructura de Depósitos Realizados con Electrodos Tubulares Revestidos de Alto Contenido de Mn (Hadfield)
Abstract: Fe-Mn-C (Hadfield) alloys for surfacing weld deposits have demonstrated excellent wear resistance under high dynamic loads. In recent years, numerous studies have been conducted to improve their wear resistance and performance through the introduction of others alloying elements. In the present work, microstructure and hardness of high Mn surfacing
Soldag. insp.. Publicado em: 09/10/2017
-
9. UM NOVO COMPLEXO HÍBRIDO FORMADO A PARTIR DE PIPLARTINA E O ÍON VANADILA: SÍNTESE, CARACTERIZAÇÃO E ESTUDO DA ATIVIDADE BIOLÓGICA
The synthesis, characterization and antimicrobial activity of novel vanadium (IV) complex derived of amide natural piplartine is reported. The minimum inhibitory concentrations (MIC) of complex, piplartine and vanadyl sulphate used in the synthesis were determined against six bacteria and one fungus. The complex exhibited good activity with minimal inhibitor
Quím. Nova. Publicado em: 2017-09
-
10. Fibroblast and pre-osteoblast cell adhesive behavior on titanium alloy coated with diamond film
It is well known that titanium alloys have mechanical strengths comparable to steels, as well as high corrosion resistance. Also, they have the advantage of promoting osseointegration, when used in medical and dental implants. This work aims to describe the adhesion properties of fibroblast and osteoblast cells on the surface of titanium aluminum vanadium al
Mat. Res.. Publicado em: 03/08/2017
-
11. Synthesis of Vanadium Interface for HFCVD Diamond Deposition on Steel Surface
Laser cladding of vanadium carbide powder developed an interlayer on AISI D6 steel as a diffusional barrier and to relief thermal residual stress. Laser cladding experiments varied resolution (DPI) and scanning speed (mm/s). CVD diamond deposition on this interface went on by HFCVD technique. The coatings were characterized by X-ray diffraction analysis (XRD
Mat. Res.. Publicado em: 06/07/2017
-
12. Annealing effects on the structural and optical properties of vanadium oxide film obtained by the hot-filament metal oxide deposition technique (HFMOD)
ABSTRACT Vanadium oxide films amorphous, nonstoichiometric and highly absorbing in the optical region were deposited on ITO-coated glass and on silicon substrates, by the hot-filament metal oxide deposition technique (HFMOD) and oxidized by ex-situ annealing in a furnace at 200, 300, 400 and 500 ºC, under an atmosphere of argon and rarefied oxygen. X-ray di
Matéria (Rio J.). Publicado em: 11/05/2017