Efecto del V y el Si Sobre la Microestructura de Depósitos Realizados con Electrodos Tubulares Revestidos de Alto Contenido de Mn (Hadfield)
AUTOR(ES)
Rodríguez, Manuel, Perdomo, Lorenzo, Béjar, Luis, Moreno, José A., Medida, Ariosto, Soriano, Juan F., Alfonso, Ismeli
FONTE
Soldag. insp.
DATA DE PUBLICAÇÃO
09/10/2017
RESUMO
Abstract: Fe-Mn-C (Hadfield) alloys for surfacing weld deposits have demonstrated excellent wear resistance under high dynamic loads. In recent years, numerous studies have been conducted to improve their wear resistance and performance through the introduction of others alloying elements. In the present work, microstructure and hardness of high Mn surfacing welds with 1.2% V and 2.4% Si additions were investigated. The surfacing welds were deposited using experimental tubular coated electrodes. Phases and micro constituents in the resulting deposits were identified using optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), hardness and micro hardness. Based on the obtained results, V additions to the alloy led to the formation of austenite as predominant phase. Besides, contributed to the formation of vanadium carbides (VC), without the presence of complex carbides. Otherwise, Si addition favored the formation of an interdendritical ferrite network. The addition of these elements favored the increase in the properties of the weld deposits, potentializing their use in applications that require high wear resistance under high loads.
Documentos Relacionados
- Efecto sobre la dilución de la granulometría de la ferroaleación en el alma de electrodos tubulares revestidos bajo la influencia de la composición del revestimiento
- Efecto del tratamiento sub-cero sobre la microestructura y dureza de fundiciones blancas alto cromo
- Efecto de la Composición Química del Metal de Aporte y del Calor Aportado Sobre la Microestructura y las Propiedades Mecánicas de Juntas Soldadas de Aceros Inoxidables Dúplex
- Comportamiento de la Resistencia al Desgaste entre Depósitos Obtenidos con Electrodos Simple y Doblemente Recubiertos
- Comportamiento del tiempo de duración, la frecuencia de los cortocircuitos y la conductividad eléctrica durante el reencendido del arco en la soldadura SMAW (AC) con electrodos E6013