37. Optical and Structural Study of ZnO Thin Films Deposited by RF Magnetron Sputtering at Different Thicknesses: a Comparison with Single Crystal
Optical characterizations of preferred orientation (002) ZnO thin films, prepared by RF magnetron sputtering under pure argon plasma, with different thicknesses have been investigated, where grain size and resistivity increase with thickness. Energy band gap and refractive indices have been calculated. A correlation between band gap values and crystalline qu
Mat. Res.. Publicado em: 16/04/2018
-
38. Preparation of Antireflective Silica Coating by the Sol-Gel Method for Heliothermic Power Plants
This work deals with the deposition of a thin layer of porous silica antireflective coating onto glass substrates. The films were deposited with different withdrawal speeds and heat-treated at 425°C for 30 minutes. The effects of heat treatment and film deposition rate on the films reflectance were evaluated. The diffuse reflectance was measured using ultra
Mat. Res.. Publicado em: 16/04/2018
-
39. Resistivity Reduction of Nanostructured Undoped Zinc Oxide thin Films for Ag/ZnO Bilayers Using APCVD and Sputtering Techniques
Nanostructured undoped zinc oxide (ZnO) thin films were deposited using atmospheric pressure chemical vapor deposition (APCVD) on glass substrates using zinc acetate dehydrate [C4H6O4Zn·2H2O, ZnAc] in less than 2 minutes for each sample. In order to reduce the resistivity of ZnO films, a very thin layer of Ag was deposited on top of the films via the sputte
Mat. Res.. Publicado em: 15/03/2018
-
40. Preparation and Characterizations of Monocrystalline Na Doped NiO Thin Films
In the present work, the effect of Na doping on optical, structural and electrical properties of Na doped NiO thin films were studied. The spray pneumatic method was used to deposit the Na doped NiO thin films in the range 0 to 5 wt.%, it are investigated at a substrate temperature of 420 °C with NiO solution 0.1 M. Firstly in the XRD specra, as found that
Mat. Res.. Publicado em: 05/03/2018
-
41. Novel Chemical Route for Deposition of Cu2ZnSnS4 Photovoltaic Absorbers
This work reports results of a study carried out to optimize the preparation conditions of Cu2ZnSnS4 (CZTS) thin films grown by sequential deposition of Cu2SnS3 (CTS) and ZnS layers, where the Cu2SnS3 compound was grown using a novel procedure consisting of simultaneous precipitation of Cu2S and SnS2 performed by diffusion membrane assisted chemical bath dep
J. Braz. Chem. Soc.. Publicado em: 2018-03
-
42. Photoluminescence of Solvent-Selected Fluorescent Moieties in MEH-PPV Solutions and Films
In this work, we examined how photoluminescence in poly[2-methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] (MEH-PPV) is affected by morphology, dictated by the mode of preparation. For that, MEH-PPV dilute solutions in good and non-solvents, thick cast films with poly[methylmethacrylate] (PMMA) as inert matrix and spin-coated thin films were prepared. Thes
J. Braz. Chem. Soc.. Publicado em: 2018-03
-
43. Structural, optical and electrical properties of Ni-doped Co3O4 prepared via Sol-Gel technique
In this article, Nickel doped Cobalt oxide thin films and powders have been prepared on glass substrates using sol gel based dip coating process in order to investigate their optical, structural and electrical properties. The Ni concentration was changed from 0 to 9 wt(%).The synthesized samples were characterised by Ultraviolete visible analysis, X-ray diff
Mat. Res.. Publicado em: 07/02/2018
-
44. Sputtering Power Induced Physical Property Variation of Nickel Oxide Films by Radio Frequency Magnetron Sputtering
NiO thin films were deposited on Si and Corning 1737 glass substrates using radio frequency (rf) magnetron sputtering system. The physical properties of NiO films under different sputtering power were thoroughly studied. The XRD results indicated that as-prepared NiO films with the sputtering power above 100 W developed only (200) preferred orientation. The
Mat. Res.. Publicado em: 01/02/2018
-
45. A New Route to Synthesize MnSe Thin Films by Chemical Bath Deposition Method
Manganese selenide (MnSe) crystalline thin film was produced with chemical bath deposition on substrates (commercial glass). Transmittance, absorption, optical band gap and refractive index were investigated by UV/VIS spectrum. The hexagonal form was observed in the structural properties in XRD. The structural and optical properties of the MnSe thin films we
Mat. Res.. Publicado em: 22/01/2018
-
46. Spray Deposited Nanostructured CuO Thin Films: Influence of Substrate Temperature and Annealing Process
In this study, CuO thin films were deposited on glass substrates at a wide range of temperatures from 450ºC to 550ºC with steps of 25ºC by chemical spray pyrolysis technique. Aiming to investigate the effect of annealing process, one of the resulting films was annealed at 450ºC for 3 hours under ambient air. Based on X-ray diffraction, all the resulting
Mat. Res.. Publicado em: 11/01/2018
-
47. ITO Obtained by Spray Pyrolysis and Coating on Glass Substrate
Conductive thin films have various applications in different technological fields. Indium tin oxide (ITO) is a mixed oxide. In the film form, ITO has been widely employed as electrode in many optoelectronic devices. Methods like thermal evaporation, sputtering, chemical vapor deposition (CVD), electron beam, spray coating, and sol-gel synthesis give ITO thin
J. Braz. Chem. Soc.. Publicado em: 2017-12
-
48. B-N Codoped p Type ZnO Thin Films for Optoelectronic Applications
The success of codoping by donor-acceptor impurities in accomplishing p type ZnO thin films deposited by spray pyrolysis technique is reported here. Monodoping ZnO with N altered the conductivity type but the resistivity is too high making it practically impossible to be useful in optoelectronic applications. B-N codoping increased the carrier concentration
Mat. Res.. Publicado em: 27/11/2017