13. Radiodensity evaluation of dental impression materials in comparison to tooth structures
In the most recent decades, several developments have been made on impression materials' composition, but there are very few radiodensity studies in the literature. It is expected that an acceptable degree of radiodensity would enable the detection of small fragments left inside gingival sulcus or root canals. OBJECTIVE: The aim of this study was to determin
Journal of Applied Oral Science. Publicado em: 2010-10
-
14. Hardness evaluation of prosthetic silicones containing opacifiers following chemical disinfection and accelerated aging
We evaluated the effects of disinfection and aging on the hardness of silicones containing opacifiers and intended for use in facial prosthetics. A total of 90 samples were produced using a cylindrical metal mold 3 mm in height and 30 mm in diameter. The samples were fabricated from Silastic MDX 4-4210 silicone in three groups: GI contained no opacifier, GII
Brazilian Oral Research. Publicado em: 2010-09
-
15. Inorganic particle analysis of dental impression elastomers
O objetivo desse estudo foi determinar quantitativamente e qualitativamente a fração de partículas inorgânicas de elastômeros dentais disponíveis comercialmente. A fração volumétrica de dois silicones por adição (Reprosil Denso/Fluído e Flexitime Denso/Fluído), três silicones por condensação (Clonage Denso/Fluído, Optosil/Xantopren, e Silon
Brazilian Dental Journal. Publicado em: 2010
-
16. Desenvolvimento de uma órtese de Dumon modificada para aplicações traqueais : um estudo experimental em cães / Development of a modified Dumon stent for tracheal applications : an experimental study in dogs
Objetivo: Descrever o desenvolvimento de uma órtese de silicone e os testes in vivo de compatibilidade e aplicabilidade na traquéia canina normal. Métodos: Quatro densidades de silicone foram testadas para a obtenção de protótipos. Para cada densidade, foi calculada a pressão exigida para causar a compressão, considerando-se uma área de contato de 1
Publicado em: 2010
-
17. Efeito de tecnicas de envelhecimento acelerado e aplicação de selante sobre a deformação permanente de reembasadores resilientes permanentes / Effect of accelerated aging and surface sealing on permanent deformation of auto-polymerizing soft liners
O objetivo neste estudo foi comparar o efeito de dois métodos de envelhecimento acelerado (termociclagem e simulação do intemperismo natural) sobre a propriedade de deformação permanente de dois reembasadores resilientes permanentes usados como forradores de próteses removíveis, um à base de silicone (UP) e outro à base resina acrílica (DF), submet
Publicado em: 2010
-
18. Reação capsular aos revestimentos de próteses mamárias de silicone texturizado e espuma de silicone em ratos
OBJETIVO: Comparar a reação capsular de dois revestimentos de próteses de silicone através da característica biofísica de aderência e dos aspectos microscópicos de reação inflamatória e formação de colágeno. MÉTODOS: Implantaram-se no dorso de 32 ratos duas membranas de silicone ambas possuindo uma superfície lisa e outra diferindo em sua est
Acta Cirurgica Brasileira. Publicado em: 2009-10
-
19. Color stability after accelerated aging of two silicones, pigmented or not, for use in facial prostheses
One of the greatest challenges faced by buccomaxillofacial prosthetists is to reproduce the patient's exact skin color and provide adequate esthetics. To reach this objective, professionals must use materials with easy characterization and that maintain color over long periods of time. The objective of this study was, thus, to evaluate the color stability of
Brazilian Oral Research. Publicado em: 2009-06
-
20. Evaluation of hardness and surface roughness of two maxillofacial silicones following disinfection
The purpose of this study was to evaluate the Shore A hardness and surface roughness of two silicones for maxillofacial prosthetic treatment, under the influence of chemical disinfection and storage. Twenty-eight specimens were obtained, half of which were made of Silastic MDX 4-4210 silicone and, the other half were made of Silastic 732 RTV silicone. The sp
Brazilian Oral Research. Publicado em: 2009-03
-
21. Avaliação do laser de baixa intensidade sobre a pseudocápsula de implantes mamários de silicone em ratos
OBJETIVO: Avaliar o efeito do laser de baixa intensidade sobre a contração da pseudocápsula que ocorre ao redor de implantes de silicone. MÉTODOS: 60 ratos machos divididos em dois grupos receberam implante de silicone. Grupo I: implante no subcutâneo da região dorsal, sem tratamento após a cirurgia; Grupo II: animais receberam sete sessões de irradi
Acta Cirurgica Brasileira. Publicado em: 2009-02
-
22. Compositos de PVC com refugos de release liners" / PVC composites with scraped release liners
Compósitos poliméricos são materiais que têm atraído cada vez maior atenção dos cientistas, assim como da indústria. "Release liners" são materiais com propriedade antiaderente utilizados para proteger a(s) face(s) adesiva(s) de uma fita adesiva, substrato e rótulos adesivos, sendo compostos basicamente de papéis revestidos de uma camada de silico
Publicado em: 2009
-
23. Avaliação dimensional de modelos de gesso em função de diferentes tecnicas e materiais de moldagem elastomericos / Dimensional evaluation of stone models in function of different techniques and elastomeric impression materials
O objetivo neste estudo foi medir e comparar a precisão dimensional de modelos de gesso confeccionados a partir de três técnicas de moldagem com dez diferentes elastômeros. Um modelo em cera, simulando um arco dental mandibular, teve retirados os dentes 44, 45 e 46 a fim de avaliar possíveis diferenças de precisão entre os lados direito e esquerdo, pe
Publicado em: 2009
-
24. Method to reduce soiling deposition on building envelope. / Método para redução de mancha nas vedações externas de edifícios.
Building roofs and façades usually show blackening surfaces after few years in large cities. On porous and silicious materials those soiling is caused by particles pollution depositions and mould growth, and the available methods available to prevent this phenomenum do not have a good performance along its service life. This thesis, based on an intensive la
Publicado em: 2009