1. Influence of the Pre-Treatments and Process Temperature on the Adhesion of TiN Films Deposited by PBII&D Over Nitrided Austenitic Stainless Steel
In this work the influence of pre-treatment cleaning processes in the adhesion of TiN films deposited by the plasma based ion implantation and deposition (PBII&D) process over plasma nitrided AISI 316L stainless steel was investigated, varying the gas composition, the duration of the sputtering process and the temperature in the same deposition chamber. The
Mat. Res.. Publicado em: 28/10/2019
-
2. Protección de acero para instrumentos quirúrgicos con recubrimientos duros en base carbono tipo DLC
ABSTRACT Martensitic stainless steels can be used in different applications such as surgical instruments where a good wear and corrosion resistance are required. Surface modification treatments such as nitriding improve the mechanical properties of these steels, however; they affect the corrosion resistance. For this reason, the DLC (Diamond Like Carbon) coa
Matéria (Rio J.). Publicado em: 19/07/2018
-
3. Estudio de los parámetros de proceso del anodizado por plasma químico en Ti-6Al-4V ELI para implantes dentales
ABSTRACT In order to study the variation effect of some parameters of micro-arc oxidation process (MAO) on Ti-6Al-4V samples for dental implants, several treatments were carried out under different conditions of current density, exposure time and electrolyte chemical composition. These processes resulted in generated bioactive titanium oxide surface coatings
Matéria (Rio J.). Publicado em: 19/07/2018
-
4. Efectos de tratamientos térmicos post-alcalinos sobre las propiedades superficiales de titanio para implantes dentales con diferentes recubrimientos
ABSTRACT Titanium is widely used as dental implant since it is bio-inert and osseointegratable. However, provided that this material cannot induce bone growth from its surface, it is usual to carry out different surface treatments in order to develop bioactive coatings that increase both the initial rate of bone development and the biological anchorage of im
Matéria (Rio J.). Publicado em: 19/07/2018
-
5. Damage Mechanisms in AISI 304 Borided Steel: Scratch and Daimler-Benz Adhesion Tests
In this study, damage mechanisms in the FeB/Fe2B coatings formed on the surface of AISI 304 steel are determined by adhesion tests. First, the boriding of the AISI 304 steel was carried out through the powder-pack method at 1223 K in the range from 2-10 h of exposure time. After treatment, Berkovich depth-sensing indentation test were conducted; the result s
Mat. Res.. Publicado em: 24/11/2015
-
6. Obtenção de revestimentos dúplex por nitretação a plasma e PVD-TiN em aços ferramenta AISI D2 e AISI H13. / Duplex coatings on AISI H13 and AISI D2 tool steels by using plasma nitriding and TiN-PVD.
In this work, the influence of both the microstructure and the load-bearing capacity of nitrided layers, formed on top of AISI D2 and AISI H13 tool steels, on adhesion and wear resistance of PVD-TiN coatings was studied. The threshold nitriding potential curves for the above mentioned steels and the optimum conditions of the pre-treatments which increased th
Publicado em: 2003