Retained Austenite
Mostrando 1-12 de 28 artigos, teses e dissertações.
-
1. Análise comparativa entre a têmpera e partição versus a têmpera e revenimento para o aço SAE 4340
RESUMO Um novo tratamento térmico tem sido pesquisado recentemente, cuja denominação é têmpera e partição (T&P), com o intuito de criar aços com austenita estável em sua microestrutura. Inicialmente, esse tratamento foi realizado em aços de alto silício, não obstante, seu potencial alcança outros diversos materiais como os de baixa liga contendo
Matéria (Rio J.). Publicado em: 16/09/2019
-
2. Effect Of The Application Of Constant And Variable Temperatures at the Overaging Stage in the Mechanical Properties of Trip780 Steel
The effect of the application of constant temperatures (isothermal plateau) and variables (cooling ramp) during the overaging (OA) stage of the continuous annealing cycle in the microstructural characteristics and mechanical properties of a TRIP steel of the class of 780 MPa was investigated. It was simulated six overaging conditions in the equipment Gleeble
Mat. Res.. Publicado em: 15/07/2019
-
3. Effects of Cold Rolling Deformation on Microstructure and Damping Capacity of a Fe-Mn-Cr-Co-Si Alloy
The microstructure evolution of Fe-19Mn-8Cr-1Co-0.2Si (wt.%) alloy and Fe-19Mn (wt.%) alloy during cold rolling and its effect on the damping capacity of the two alloys were investigated. It was shown that the damping capacity of the two alloys was enhanced significantly owing to the deformation-induced ε-martensite and stacking faults. The Fe-19Mn-8Cr-1Co-
Mat. Res.. Publicado em: 11/07/2019
-
4. 3D Microstructural Finite Element Simulation of Martensitic Transformation of TRIP Steels
Abstract In this paper the effects of deformation modes on martensitic transformation for TRIP steels which are composed of Ferrite, Bainite and Retained austenite are investigated in the view of the microstructural level. For this porpose the simulations are run for a synthetically generated microstructure which have 55% Ferrit, 35% Bainite and 10% Retained
Lat. Am. j. solids struct.. Publicado em: 30/07/2018
-
5. Estabilidad de la austenita retenida bajo condiciones de deformación en aceros multifásicos con bainita nanoestructurada
ABSTRACT A steel with nominal composition 0.25C, 1.9Si, 0.63Mn, 1.5Cr was manufactured using an induction furnace. The as-cast alloy was homogenized and the temperatures of austenite start (AC1) and finish (AC3) during heating were determined by dilatometric analyses. Two intercritical austenitization temperatures were selected, which were used to perform pa
Matéria (Rio J.). Publicado em: 19/07/2018
-
6. Estudio de la microestructura de un cordón de soldadura de un acero P91 mediante microscopía electrónica de transmisión
ABSTRACT In the present work the microstructural characterization of a single-pass weld of 9Cr1MoVNb P91 steel performed by the flux-cored arc welding (FCAW) process in the “as welding” condition has been carried out by means of transmission electron microscopy. P91 steel offers a good weldability, but the mechanical properties of the welded joints are f
Matéria (Rio J.). Publicado em: 19/07/2018
-
7. Efecto del tratamiento sub-cero sobre la microestructura y dureza de fundiciones blancas alto cromo
ABSTRACT The effect of the sub-zero treatment temperature on the transformation of retained austenite to martensite in two high chromium white cast irons (ASTM A532 Class II Type B) was studied. The sub-zero treatment applied to each alloy in the as cast condition was performed at -40, -65 and -180 ° C for 10 minutes; after the holding time was completed th
Matéria (Rio J.). Publicado em: 19/07/2018
-
8. Determinación de los parámetros de austenización intercrítica para el desarrollo de aceros multifásicos mediante análisis dilatométrico
ABSTRACT The Multiphase steels are materials with exceptional mechanical properties including high strength, excellent ductility and hardening coefficient and good conformability. These properties are related with the microstructure, which can be a combination of ferrite and martensite (Dual phase steels) or more complex microstructures with ferrite, bainite
Matéria (Rio J.). Publicado em: 19/07/2018
-
9. Microstructural Evolution and Phase Transformation in Laser Cladding of Cr and Mo Powder on Grey Cast Iron: Mixture Design of Experiment (DOE)
Laser cladding on grey cast iron at high power processing was investigated for microstructural evolution and phase transformation to enhance surface properties. Cladding was designed using a mixture of DOE with peak power (Pp) and pulse repetition frequency (PRF), and a mixture component of Cr and Mo ratio as factors. Microstructural findings indicated absol
Mat. Res.. Publicado em: 21/11/2017
-
10. Microstructure and Mechanical Properties of ASTM A743 CA6NM Steel Welded by FCAW Process
CA6NM steel is widely used in the manufacture of hydraulic turbines metallic parts, due to its resistance to corrosion and cavitation damage, combined with good weldability and fatigue properties. However, welding of this type of steel is complex and to ensure a minimum residual stress after welding it is necessary perform a post welding heat treatment (PWHT
Mat. Res.. Publicado em: 21/09/2017
-
11. Tribocorrosion and Electrochemical Behavior of DIN 1.4110 Martensitic Stainless Steels After Cryogenic Heat Treatment
DIN 1.4110 martensitic stainless steel is largely used in the cutlery industry due to its high corrosion resistance associated with high mechanical resistance. However, when this material works under corrosion and wear conditions at the same time, their synergistic effect can accelerate the degradation process of the alloy. Cryogenic heat treatments have bee
Mat. Res.. Publicado em: 23/02/2017
-
12. Softening Mechanisms of the AISI 410 Martensitic Stainless Steel Under Hot Torsion Simulation
This study investigated the softening mechanisms of the AISI 410 martensitic stainless steel during torsion simulation under isothermal continuous in the temperature range of 900 to 1150 °C and strain rates of 0.1 to 5.0s-1. In the first part of the curves, before the peak, the results show that the critical (εc) and peak (εp) strains are elevated for hig
Mat. Res.. Publicado em: 23/01/2017