Softening Mechanisms of the AISI 410 Martensitic Stainless Steel Under Hot Torsion Simulation
AUTOR(ES)
Oliveira, Thiago Santana de, Silva, Eden Santos, Rodrigues, Samuel Filgueiras, Nascimento, Carmem Célia Francisco, Leal, Valdemar Silva, Reis, Gedeon Silva
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
23/01/2017
RESUMO
This study investigated the softening mechanisms of the AISI 410 martensitic stainless steel during torsion simulation under isothermal continuous in the temperature range of 900 to 1150 °C and strain rates of 0.1 to 5.0s-1. In the first part of the curves, before the peak, the results show that the critical (εc) and peak (εp) strains are elevated for higher strain rate and lower temperatures contributing for higher strain hardening rate (h). Moreover, this indicated that dynamic recrystallization (DRX) and dynamic recovery (DRV) are not effective in this region. After the peak, the reductions in stresses are associated to the different DRX/DRV competitions. For lower temperatures and higher strain rates there is a delay in the DRX while the DRV is acting predominantly (with low Avrami exponent (n) and high t0.5). The steady state was reached after large strains showing DRX grains, formation of retained austenite and the presence of chromium carbide (Cr23C6) and ferrite δ at the martensitic grain boundaries. These contribute for impairing the toughness and ductility on the material. The constitutive equations at the peak strain indicated changes in the deformation mechanism, with variable strain rate sensitivity (m), which affected the final microstructure.
Documentos Relacionados
- Modificação e caracterização da superfície do aço inoxidável Martensítico AISI 410
- Nitriding using cathodic cage technique of martensitic stainless steel AISI 420 with addition of CH4
- Phase transformations in an AISI 410S stainless steel observed in directional and laser-induced cooling regimes
- Fracture Modes of AISI Type 302 Stainless Steel Under Metastable Plastic Deformation
- Mechanically Induced Martensitic Transformation of Hot Rolled and Annealed 304L Austenitic Stainless Steel at Room and Cryogenic Temperatures