1. Aqueous Extract of Cumaru (Dipteryx odorata) Seeds as Corrosion Inhibitor for Mild Steel in Hydrochloric Acid Solution
The corrosion inhibition of mild steel by aqueous extract of cumaru (Dipteryx odorata) seeds and its high molecular weight fraction (HMWF) was investigated in 1 mol L-1 HCl solution. The study was carried out through gravimetric essays, open circuit potential measurements, anodic and cathodic polarization curves and electrochemical impedance analyses, as wel
J. Braz. Chem. Soc.. Publicado em: 2021-02
-
2. Aqueous Extracts of the Castor Beans as a Corrosion Inhibitor of Mild Steel in HCl Media
The present work studied aqueous extracts of castor beans as a natural inhibitor of the corrosion of mild steel in 1 M HCl using gravimetric tests, potentiodynamic polarization curves, linear polarization method, electrochemical impedance measurements, surface analysis by scanning electron microscopy (SEM) and chemical characterization by Fourier transform i
J. Braz. Chem. Soc.. Publicado em: 2020-06
-
3. Effect of Ca Content on Properties of Extruded Mg-3Zn-0.5Sr-xCa Alloys for Medical Applications
Mg-3Zn-0.5Sr-xCa(wt.%) (x=0, 0.2, 0.5) alloys were fabricated by casting and hot extrusion. X-ray diffraction (XRD) and optical microscopy observation showed that the microstructure of Mg-3Zn-0.5Sr-xCa alloys was composed of α-Mg matrix and Mg17Sr2 phase precipitated along grain boundaries. The tensile strength of the alloy increased from 255MPa to 305MPa w
Mat. Res.. Publicado em: 30/09/2019
-
4. Corrosion Behavior of 316L and Alloy 182 Dissimilar Weld Joint with Post-Weld Heat Treatment
ABSTRACT Austenitic stainless steel and nickel-base alloys welds are widely used in nuclear reactor components, plants of energy generation, chemical, and petrochemical industries, due to their high corrosion resistance. The post weld heat treatments (PWHT) are generally applied to welding in order to relieve the welding residual stress. The aim of this work
Matéria (Rio J.). Publicado em: 16/09/2019
-
5. EFFECT OF THE NATURE OF THE ELECTROLYTE AND THE NATURE OF THE INTERFACE ON THE HYDROGEN EVOLUTION POTENTIAL: EXPERIMENTS FOR CHEMISTRY STUDENTS
This work presents an experiment done for chemistry students about the effect of the nature of the electrolyte and the nature of the interface on the hydrogen evolution reaction by electrolysis. Two techniques are suggested: method A - two identical copper electrodes in a direct current circuit and method B - three different electrodes in a dc potentiostatic
Quím. Nova. Publicado em: 27/05/2019
-
6. Comportamento da corrosão microbiológica do aço duplex com aplicação de sais de quaternário de amônio
RESUMO A corrosão microbiológica tem causado diversos prejuízos para variados segmentos industriais que utilizam os materiais metálicos em seus sistemas. Uma forma de minimizar e até mesmo controlar os problemas causados pela corrosão microbiológica tem sido a aplicação de biocidas nestes sistemas. Neste trabalho, a corrosão microbiológica do aço
Matéria (Rio J.). Publicado em: 20/05/2019
-
7. Effect of Sn Addition in the Microstructure Refinement and Corrosion Resistance of Cu-Zr-Al-Ag Alloy
In this paper, a composition of known high glass-forming ability, Cu42Zr42Al8Ag8 and a novel Cu42Zr42Al8Ag4Sn4, were produced by suction-casting. After rapid solidification of both alloys, X-ray diffraction patterns along with crystallite size estimation by Scherrer equation and scanning electron microscopy images revealed a refined microstructure, composed
Mat. Res.. Publicado em: 04/04/2019
-
8. Barley Agro-industrial Residues as Corrosion Inhibitor for Mild Steel in 1mol L-1HCl Solution
The corrosion inhibition of mild steel in 1 mol L−1HCl by barley grains and malting process residue extracts was investigated by weight loss measurements, polarization curves, electrochemical impedance measurements and scanning electron microscopy. The inhibition efficiency exceeded 92% in the presence of 100 mg L−1 extracts after 24 h immersion time for
Mat. Res.. Publicado em: 01/04/2019
-
9. The Modification of (Nd0.5Ta0.5)4+ Complex-Ions on Structure and Electrical Properties of Bi0.5Na0.5TiO3-BaTiO3 Ceramics
The (Bi0.5Na0.5)0.94Ba0.06Ti1-x (Nd0.5Ta0.5) xO3 (0.01≤x≤0.05) lead-free ceramics (BNBT-xNT) used (Nd0.5Ta0.5)4+ complex-ions to modify its structure and electrical properties. The BNBT-xNT ceramics exhibit the coexistence of tetragonal and rhombohedral phase. The (Nd0.5Ta0.5)4+ complex-ions prohibit grain growth, and its average grain size decreases fro
Mat. Res.. Publicado em: 14/03/2019
-
10. Experimental and Theoretical Study of Corrosion Inhibition of Mild Steel in 1.0 M HCl Medium by 2(-4( hloro phenyl-1H- benzo[d]imidazol)-1-yl)phenyl)methanone
The 2(-4(chloro phenyl-1H- benzo[d]imidazol)-1-yl)phenyl)methanone (CBIPM) was synthesized and tested as a corrosion inhibitor for mild steel in 1.0 M HCl solution using electrochemical and spectroscopy measurements. Results obtained showed that this compound has a good inhibition properties for mild steel corrosion in acidic medium which its inhibition effi
Mat. Res.. Publicado em: 06/12/2018
-
11. Evaluation of Corrosion Resistance of Commercial Aluminum Alloys in Ethanol Solutions
In the present research, we studied the corrosion resistance of commercial aluminum alloys exposed to ethanol produced in the northeastern region of Argentina and to commercial ethanol as reference medium. Electrochemical tests of potentiodynamic polarization and weight loss were performed by immersion at temperatures below the boiling point of ethanol (25 �
Mat. Res.. Publicado em: 22/10/2018
-
12. Electrochemical corrosion characterization of nickel aluminides in acid rain
ABSTRACT Nickel aluminides have been extensively studied in recent decades to replace superalloys, in some components of aircraft turbines, because they have excellent corrosion resistance. Many industrial cities have the problem of air pollution, which has forced the study of the degradation of these alloys in the presence of acid rain. The aim of this work
Matéria (Rio J.). Publicado em: 19/07/2018