Mcm 41
Mostrando 25-36 de 111 artigos, teses e dissertações.
-
25. Kinetic study of the catalytic pyrolysis of elephant grass using Ti-MCM-41
This work aimed to study the kinetics of thermal and catalytic pyrolysis using Ti-MCM-41 as catalyst in order to assess the catalytic pyrolysis efficiency compared to thermal pyrolysis of elephant grass. Ti-MCM-41 molecular sieve was synthesized by hydrothermal method from hydrogel with the following molar composition:1.00 CTMABr: 4.00 SiO2:X TiO2: 1 + X Na2
Mat. Res.. Publicado em: 05/08/2014
-
26. Catálise básica usando sílica mesoporosa estabilizada por acrilatos encapsulados
The synthesis of new type of silicas, with structures akin to that of MCM-41, containing polyacrylate-encapsulated micelles in their mesopores is reported. Initially, the monomers were inserted in the aqueous micelles of cetyltrimethylammonium cations. MCM-41 was then prepared in this microemulsion. Finally, the polymerization of the acrylates was initiated
Quím. Nova. Publicado em: 2014-06
-
27. Effects of impregnation methods and drying conditions on quinoline hydrodenitrogenation over Ni-W based catalysts
Os efeitos dos métodos de impregnação (co-impregnação e impregnação sequencial) e das condições de secagem (ar e vácuo) sobre estrutura e o comportamento catalítico de catalisadores Ni-W suportados em MCM-41 foram investigados. Os catalisadores foram caracterizados por difratometria de raios X de pó (XRD), espectroscopia de absorção no infraver
J. Braz. Chem. Soc.. Publicado em: 2014-04
-
28. A new functionalized MCM-41 mesoporous material for use in environmental applications
Este trabalho descreve a síntese e caracterização de um novo adsorvente mesoporoso que consiste o MCM-41 funcionalizado com o ácido p-aminobenzóico modificado (PABA-Si). A síntese foi realizada pelo método hidrotermal/co-condensação. O PABA-MCM-41 foi caracterizado usando FTIR, SAXS, adsorção/desorção de N2, MEV e TG. Os experimentos em batelada
J. Braz. Chem. Soc.. Publicado em: 2014-02
-
29. Adsorção de CO2 em peneiras moleculares micro e mesoporosas
Microporous molecular sieves of type Y, Beta, ZSM-5, ZSM-12 and ZSM-35, and mesoporous molecular sieves of type MCM-41 and MCM-48, and these sieves modified with triethanolamine and ethylenediamine were obtained and characterized by XRD, FTIR, TGA and nitrogen adsorption. The adsorption tests were performed by the gravimetric method under a stream of CO2 at
Quím. Nova. Publicado em: 2014
-
30. Immobilization of cobalt phthalocyanine and tetrasulfophthalocyanine onto MCM-41 and MCM-48: effect of immobilization method on catalytic activity
Tetra-sulfoftalocianina de cobalto (CoPcS) foi ancorada quimicamente à superfície das MCM-41 e MCM-48 modificadas com aminas. Estas sílicas mesoporosas foram preparadas por processo hidrotérmico. Misturas físicas de CoPc em MCM-41 e em MCM-48 também foram preparadas para fins de comparação. Os quatro catalisadores preparados, 10 wt.% CoPcS/NH2-MCM-41
J. Braz. Chem. Soc.. Publicado em: 2013-11
-
31. Textural properties of nickel, palladium and titanium oxides supported on MCM-41 materials and their application on oxidative desulfurization of dibenzothiophene
Textural and catalytic properties of nickel, palladium or titanium oxides supported on MCM-41 materials were evaluated in this paper. The results indicated that the MCM-41 material with well defined and highly ordered hexagonal structure was obtained. After metal ions impregnation and calcinations, the structure of MCM-41 was preserved and formed metallic ox
Mat. Res.. Publicado em: 27/09/2013
-
32. Emprego da cinza da casca de arroz como única fonte de sílica na formação de materiais mesoporosos
Este trabalho relata o estudo da síntese de peneiras moleculares semelhantes à MCM-41, empregando cinza da casca de arroz como única fonte de sílica. Para critérios de comparação uma síntese foi realizada com sílica comercial aerosil 200. A sílica da casca de arroz foi obtida mediante tratamento térmico a 600 ºC e lixiviação em refluxo por 2 h
Cerâmica. Publicado em: 2013-03
-
33. Síntese do material mesoporoso MCM-41 usando esponja de água-doce como fonte de sílica
Fresh water sponge was used as a silica source for the synthesis of MCM-41 via the hydrothermal process. The silica was extracted from the sponge by washing with nitric acid and piranha solution. Synthesis of MCM-41 was performed at 100 °C for 5 days and the procedure was optimized, with modifications made to the leaching temperature of the silica and the s
Quím. Nova. Publicado em: 2013
-
34. AVALIAÇÃO DA VERSATILIDADE DO MCM-41 FUNCIONALIZADO. / EVALUATION OF VERSATILITY OF MCM-41 FUNCTIONALIZED.
Neste trabalho, o material mesoporoso MCM-41 foi funcionalizado com 3-aminopropilmetoxisilano (APTS) para diversas finalidades como, adsorção do corante vermelho de remazol, imobilização de íons lantanídeos (Eu+3, Tb+3 ou Gd+3), coordenação com o ácido 2,6-piridina-dicarboxílico (dpa) e imobilização do complexo [RuCl2(PPh3)2(Meo-bipy)]. As propri
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 31/07/2012
-
35. DESENVOLVIMENTO DE PENEIRAS MOLECULARES MESOPOROSAS DO TIPO MCM-41 E MCM-48 IMPREGNADAS COM AMINAS PARA UTILIZAÇÃO NA ADSORÇÃO DE CO2. / DEVELOPMENT OF TYPE MESOPOROUS MOLECULAR SIEVES MCM-41 AND MCM-48 IMPREGNATED WITH AMINES FOR USE IN ADSORPTION CO2.
O aumento significativo das emissões de dióxido de carbono na atmosfera vem acentuando o efeito do aquecimento global. A busca por fontes energéticas que minimizem as emissões é de grande importância, como também o uso de ações complementares como processos para captura deste gás das principais fontes emissoras. Dentre alguns processos já bem conh
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 25/07/2012
-
36. Sílicas mesoporosas HMS e MCM-41 modificadas com grupos contendo nitrogênio e enxofre como adsorventes para íons metálicos em solução. / Mesoporous silica modified with groups containing nitrogen and sulfur as adsorbents for metal ions in solution.
Híbridos mesoporosos orgânico-inorgânicos são candidatos promissores na área de adsorção. Neste trabalho, foram sintetizados novos adsorventes baseados em sílicas mesoporosas do tipo HMS e MCM-41 organofuncionalizadas com grupos contendo nitrogênio e enxofre empregando o método pós funcionalização. A sílica HMS foi obtida a partir do direcionad
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 01/06/2012