Síntese do material mesoporoso MCM-41 usando esponja de água-doce como fonte de sílica

AUTOR(ES)

Lacerda Júnior, Orivaldo da Silva, Cavalcanti, Rodrigo Marinho, Matos, Thaisa Moreira de, Venâncio, Jocilândia de Brito, Barros, Iuri Bezerra de, Veiga-Júnior, Valdir Florêncio da, Barros, Ivoneide de Carvalho Lopes

FONTE

Quím. Nova

DATA DE PUBLICAÇÃO

2013

RESUMO

Fresh water sponge was used as a silica source for the synthesis of MCM-41 via the hydrothermal process. The silica was extracted from the sponge by washing with nitric acid and piranha solution. Synthesis of MCM-41 was performed at 100 °C for 5 days and the procedure was optimized, with modifications made to the leaching temperature of the silica and the synthesis of mesoporous material, which was characterized by XRD, FT-IR, SEM and adsorption of N2. The optimal result was achieved at a temperature of 135 °C for 3 days, showing ordered mesoporous material with a surface area of 1080 m² g-1.

Documentos Relacionados

• Mercúrio total em pescado de água-doce
• Síntese e impregnação de peneiras moleculares Fe MCM-41 derivada de sílica da casca do arroz
• Síntese e caracterização de peneiras moleculares mesoporosas do tipo MCM-41 e AlMCM-41 a partir de fontes alternativas de sílica e de alumínio
• Síntese, caracterização e aplicação do MCM-41 e A1-MCM-41 na pirólise do resíduo atmosférico de petróleo
• AVALIAÇÃO DA VERSATILIDADE DO MCM-41 FUNCIONALIZADO.