13. Rice Husk Reuse in the Preparation of SnO2/SiO2Nanocomposite
In this study, biogenic SiO2 of high purity and high surface area obtained from rice husk was used for prepare a nanostructured SnO2/SiO2composite. The predominantly amorphous silica was extracted in an acidic route and then the nanocomposite was done via sol-gel route using ethylene glycol and citric acid followed by heat treatment. SiO2 content of the rice
Mat. Res.. Publicado em: 2015-06
-
14. Radiant exposure effects on physical properties of methacrylate - and silorane-composites
AIM: To evaluate the effect of different radiant exposures on the degree of conversion (DC), Knoop hardness number (KHN), plasticization (P), water sorption (WS), and solubility (S) of different monomer resin-based composites. METHODS: Circular specimens (5 x 2 mm) were manufactured from methacrylate and silorane composite resins, and light-cured at 19
Braz. J. Oral Sci.. Publicado em: 2014-09
-
15. Effects of impregnation methods and drying conditions on quinoline hydrodenitrogenation over Ni-W based catalysts
Os efeitos dos métodos de impregnação (co-impregnação e impregnação sequencial) e das condições de secagem (ar e vácuo) sobre estrutura e o comportamento catalítico de catalisadores Ni-W suportados em MCM-41 foram investigados. Os catalisadores foram caracterizados por difratometria de raios X de pó (XRD), espectroscopia de absorção no infraver
J. Braz. Chem. Soc.. Publicado em: 2014-04
-
16. Effects of various hydrogen peroxide bleaching concentrations and number of applications on enamel
AIM: To evaluate the effects of three hydrogen peroxide (HP) concentrations on enamel mineral content (MC), following three peroxide applications and using three methods to measure the MC. METHODS : Forty samples were obtained from bovine incisors and randomly divided into 4 groups (n=10). The control group remained untreated, while the experimental gro
Braz. J. Oral Sci.. Publicado em: 2014-03
-
17. FT-Raman spectroscopic study of skin wound healing in diabetic rats treated with Cenostigma macrophyllum Tul
INTRODUCTION: Patients with diabetes mellitus exhibit a delay in the lesion repair process. The active components of Cenostigma macrophyllum may represent a viable alternative to facilitate the recovery of these lesions. The aim of this study was to evaluate the effects of emulsion oil-water Cenostigma macrophyllum in the repair process of lesions in rats wi
Rev. Bras. Eng. Bioméd.. Publicado em: 2014-03
-
18. Biopolymer-clay nanocomposites: cassava starch and synthetic clay cast films
Nanocompósitos à base de amido de mandioca, argila sintética hectorita e açúcar invertido (plastificante) foram preparados por processo em meio aquoso (casting) produzindo filmes transparentes e homogêneos. Pequenas quantidades de argila (5-15% em massa) produzem principalmente nanocompósitos esfoliados, enquanto grandes quantidades (30% em massa) pro
J. Braz. Chem. Soc.. Publicado em: 2014-02
-
19. Evaluation of inorganic and organic bone components after application of an apatite-coated Al2O3 implants as scaffolds for bone repair
The aim of this work was to study the influence of uncoated and apatite-coated Al2O3 implants on bone regeneration after 30 days of surgery in New Zealand white rabbits. Twelve samples of Al2O3 implants were prepared and half of them (n = 6) were apatite-coated by the modified biomimetic method. Three experimental groups were tested as Group C - control, sur
Braz. arch. biol. technol.. Publicado em: 31/01/2014
-
20. Molecular and Structural Evaluation of Dentin Caries-Like Lesions Produced by Different Artificial Models
Este estudo avaliou as características estruturais e moleculares da lesão de cárie artificial em dentina produzidas por diferentes modelos artificiais (LCA) comparados à lesão de cárie natural (LCN). Cento e vinte e quatro blocos de dentina oclusal hígida e 47 blocos cariados foram obtidos e a dureza superficial foi analisada (SH1). Eles foram dividid
Braz. Dent. J.. Publicado em: 2013-12
-
21. Síntese pelo método da coprecipitação e caracterização estrutural do tungstato de cálcio com estrutura tipo scheelita
Nanocristais de CaWO4 foram sintetizados pelos métodos de coprecipitação com diferentes razões do solvente (água/etilenoglicol) e processados à temperatura ambiente. Estes nanocristais foram caracterizados por difração de raios X, espectroscopia Raman, espectroscopia na região do infravermelho com transformada de Fourier (FT-IR) e espectrofotometria
Cerâmica. Publicado em: 2013-09
-
22. Characterization of ZSM-5 modified with niobium pentoxide: the study of thiophene adsorption
Adsorventes ZSM-5 impregnados com Nb2O5 foram aplicados na remoção de enxofre sob a forma de tiofeno, substância refratária de difícil remoção dos combustíveis líquidos. Para tanto, foi preparado um combustível modelo contendo iso-octano contaminado com tiofeno nas concentrações de 877,5 a 1155 ppmw. As amostras foram caracterizadas por difratome
J. Braz. Chem. Soc.. Publicado em: 2013-01
-
23. Estudo teórico das propriedades ópticas dos BaWO4 e PbWO4 / Theoretical Study of the optical properties of BaWO4 e PbWO4
Dentre as scheelitas, podemos destacar os Tungstato de Bário (BaWO4) e Tungstato de Chumbo (PbWO4). Estes compostos podem ser sintetizados por várias rotas de síntese. No entanto, podemos destacar a síntese pelo método hidrotérmico assistido por microondas (SHM). Com o uso dessa técnica, podem-se utilizar diversos solventes, agentes surfactantes e con
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 21/09/2012
-
24. Interação de forsterita-91 e da cisteína em condições de química prebiótica utilizando diferentes técnicas espectroscópicas, químicas e mineralógicas
This work simulated prebiotic conditions existed on primordial Earth and studiedthe interaction between forsterite-91, cysteine and artificial seawater. These interactions were studied in aqueous medium at two values of pH 2.0 and 8.0. The samples of olivine plus distilled water and artificial seawater were mixed for 24h, centrifuged, the solids and supernat
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 10/02/2012