Dynamic Recrystallization
Mostrando 1-12 de 28 artigos, teses e dissertações.
-
1. Double Identification of the Optimal Hot Deformation Parameter Windows for AlCu4SiMg Alloy
In order to achieve hot processing products with expected microstructures, the construction of corresponding relationships between micro-evolution mechanisms and hot processing parameters is essential. In this study, such corresponding relationships of as-cast AlCu4SiMg alloy were constructed by double evaluating processing maps and Zener-Holloman (Z) parame
Mat. Res.. Publicado em: 10/07/2019
-
2. Effect of Processing Parameters on Hot Deformation Behaviour and Microstructural Evolution of PM Ti-5553 Alloy at a Moderate-high Strain Rate
Isothermal compression tests of Ti-5553 (Ti-5Al-5V-5Mo-3Cr) alloy, produced by a fast consolidation approach from blended elemental powder mixture, were performed on a Gleeble® 3800 thermal-physical simulator to investigate its hot deformation behaviour. The samples were compressed in a wide temperature range from 700 ºC to 1150 ºC and a moderate-high str
Mat. Res.. Publicado em: 10/06/2019
-
3. Efecto del cambio en el camino de deformación en la formabilidad de chapas de acero DP-780 y zinc Zn20
ABSTRACT The Forming Limit Diagram (FLD), frequently used to characterize the formability of sheet metals, is determined by assuming proportional loading histories up to the onset of necking. However, the limit strains are highly affected by strain-paths changes, which are very usual in real metal forming processes. The aim of this work is to analyze the eff
Matéria (Rio J.). Publicado em: 19/07/2018
-
4. Application of Friction Surfacing to the Production of Aluminum Coatings Reinforced with Al2O3 Particles
The aim of this work was to produce deposits of AA6351-T6, reinforced with alumina (Al2O3) particles, over a substrate of AA5052-H32 through friction surfacing. AA6351-T6 consumable rods were drilled with one and two holes, which were filled with Al2O3 particles posteriorly. To perform the deposition, a conventional KONE KFE-3/BR milling machine was used. Th
Mat. Res.. Publicado em: 13/11/2017
-
5. Recovery Mechanisms in a Compressed Ni-Ti Superelastic Alloy
The present work studied the influence of annealing on a Ni-Ti alloy submitted to uniaxial compression. The stress-strain curve under compression showed the absence of the Stress-Induced-Martensite (SIM) plateau and 42% of remaining austenitic phase (B2). identified by the Electron Backscattered Diffraction (EBSD) technique on a Scanning Electronic Microscop
Mat. Res.. Publicado em: 19/10/2017
-
6. Softening Mechanisms of the AISI 410 Martensitic Stainless Steel Under Hot Torsion Simulation
This study investigated the softening mechanisms of the AISI 410 martensitic stainless steel during torsion simulation under isothermal continuous in the temperature range of 900 to 1150 °C and strain rates of 0.1 to 5.0s-1. In the first part of the curves, before the peak, the results show that the critical (εc) and peak (εp) strains are elevated for hig
Mat. Res.. Publicado em: 23/01/2017
-
7. Identification for the Optimal Working Parameters of Ti-6Al-4V-0.1Ru Alloy in a Wide Deformation Condition Range by Processing Maps Based on DMM
The hot deformation behaviours of Ti-6Al-4V-0.1Ru alloy were investigated by isothermal hot compression tests in the temperature range of 1023-1423 K and strain rate range of 0.01-10 s-1. The β transus was determined to be 1198 K by continuous heating method. The values of deformation activation energy Q at the strain of 0.3 were calculated to be 630.01 kJ/
Mat. Res.. Publicado em: 10/11/2016
-
8. Friction stir welding of duplex and superduplex stainless steels and some aspects of microstructural characterization and mechanical performance
Friction stir welding was used to produce butt joints on 6 mm thick plates of UNS S32101 lean duplex stainless steel, S32205 duplex stainless steel, and S32750 and S32760 superduplex stainless steels. Fully consolidated joints were achieved, with full penetration, using heat input of 1.37-1.50 kJ/mm. Specimens submitted to tensile testing performed perpendic
Mat. Res.. Publicado em: 12/02/2016
-
9. Microstructure and Mechanical Properties of Severely Deformed Mg-4.5Al-1.0Zn Alloy Processed by Asymmetric Rolling on Ingot and Twin Roll Cast Strip
The twin roll cast Mg-4.5Al-1.0Zn alloy sheets, processed by asymmetric rolling and subsequent annealing were investigated. The asymmetric rolling on Mg-4.5Al-1.0Zn ingot was also studied for comparison in terms of microstructure, texture and mechanical properties of the sheets. The results can be summarized as follows. The rolled sheets show intensively def
Mat. Res.. Publicado em: 05/02/2016
-
10. Estudo do comportamento termomecânico do aço API 5L X80 microligado ao Nb-Ti através de ensaios de torção a quente
AbstractThe controlled rolling of high strength low alloy steel has been widely used in the production of large diameter pipes for the oil and gas industry. The thermo-mechanical control process (TMCP) is used to maximize grain refinement and achieve both higher strength and toughness in the steels. In this sense, API 5L X80 micro-alloyed Nb-Ti steel was sub
Rem: Rev. Esc. Minas. Publicado em: 2015-06
-
11. A characterization for the constitutive relationships of 42CrMo high strength steel by Artificial Neural Network and its application in isothermal deformation
In hot working process, the prediction of material constitutive relationship can improve the optimization design process. Recently, the artificial neural network models are considered as a powerful tool to describe the elevated temperature deformation behavior of materials. Based on the experimental data from the isothermal compressions of 42CrMo high streng
Mat. Res.. Publicado em: 05/08/2014
-
12. Extrusion-shear of AZ31 alloy billets with low temperature and high speed by using three-dimensional finite element modeling and experiments
A new kind of compound extrusion technology including direct extrusion and shears for AZ31 magnesium billets can cause plastic large deformations and high strain rates. A series of compressive tests have been done to obtain the stress-strain curves of AZ31 magnesium alloy. Three-dimensional (3D) thermo-mechanical coupled finite element modeling of forming ma
Mat. Res.. Publicado em: 28/07/2014