37. Efeito da base de cimento de ionômero de vidro modificado por resina e técnicas de inserção de resina composta na interface dentina/restauração adesiva / Effect of resin-modified-glass-ionomer linning and composite placement on adhesive interface
The aim of this study was to evaluate the effect of resin-modified-glassionomer linning and incremental technique on the bond strength of the composite restoration interface. Methods: Cavities were made (4.5mm X 3mm X 5mm) in 52 extracted human molars, divided into 4 groups: Group 1 (control) no linning + two horizontal increments (C Factor = 5); Group 2: no
Publicado em: 2011
-
38. Influence of the photoinitiator system and light photoactivation units on the degree of conversion of dental composites
The aim of this study was to observe the influence of two light polymerization units (LED or halogen light) on the degree of conversion (DC) of three dental composites with lighter shades and a different photoinitiator system. The top (T) and bottom (B) surfaces of 60 discs of composite resin (Filtek™ Supreme, Filtek™ Z250, Tetric™ Ceram Bleach) cured
Brazilian Oral Research. Publicado em: 2010-12
-
39. Analysis of polymerization time on abrasive wear of dental resins
An evaluation was made of the abrasive wear of six composite thermofixed dental resins subjected to different polymerization times. The method of evaluation was based on sharpness measurements to quantify the abrasive wear resistance of the resins. To this end, a test bench was built, consisting of a rotating porcelain cylinder that wears out a resin-coated
Materials Research. Publicado em: 2010-03
-
40. Study and optimization of photocuring processes of composite resins to dental jobs. / Estudo e otimização da fotocura de resinas compostas de emprego odontológico
The aim of this study was to investigate the optimization of photo-cure of dental composite resin by combined curing methods. The curing was performed associating ultrasound and LED and LED with pre-heating composite resin. The irradiation performed was centered at 470 nm with power density of 600 mW/cm2 for the ultrasound and pre-heating association. The ap
Publicado em: 2010
-
41. Alterações nas caracteristicas da superficie de compositos restauradores sumetidas a diferentes tecnicas de acabamento e polimento / Changes in surface characteristics of restorative composites subjected to different techniques for finishing and polishing
Several changes were made in the light-cured composites resins manufacture, especially trying to obtain better color stability, adequate wear resistance and clinically acceptable surface smoothness. About this, manufacturers have predominantly reduced the diameter of charged particles, promoting changes in its geometry and also incorporating a bigger amount
Publicado em: 2010
-
42. Surface roughness analysis of acrylic resin for provisional crowns under different commercial brands / Análise da rugosidade superficial de diferentes marcas comerciais de resina acrílica para coroas provisórias
Provisional crowns have some features that may compromise aesthetics and favors adherence of microorganisms and dental plaque formation. Previous studies have shown that processing may influence roughness and porosity of acrylic resins commonly used make provisional crowns. Because the several commercial resins available present differences in their quality
Publicado em: 2010
-
43. Efeito da escovação e enxaguatório bucal na alteração de cor e rugosidade de resinas compostas / Effect of toothbrushing and mouthwash on the color change and surface roughness of composite resins.
The present study evaluated in vitro the influence of different types of mouthwash associated with brushing, the color change and surface roughness of different types of direct composite resins (M1 - Filtek Supreme XT, M2 - Z100, M3 - Ice) through a PCB 6807 spectrocolorimeter of BYK-Gradner, rugosimeter model Mitutoyo SJ-201P and scanning electron microscop
Publicado em: 2010
-
44. Estudo do processo de difusão em resinas dentárias / Study of diffusion process in dental resins
Atualmente os fabricantes de resinas odontológicas visam obter uma resina que possa associar maior durabilidade, com uma efetiva ligação dentina-resina. As resinas dentárias podem absorver água e produtos químicos do ambiente, além de liberar componentes para os ambientes circunvizinhos. A intrusão de água no material dentário pode ocasionar deteri
Publicado em: 2010
-
45. EFEITO DE AGENTES CLAREADORES À BASE DE PERÓXIDO DE HIDROGÊNIO SOBRE A FLUORESCÊNCIA DE RESINAS COMPOSTAS / EFFECT OF HYDROGEN PEROXIDE BLEACHING AGENTS ON FLUORESCENCE OF COMPOSITE RESINS
Devido à crescente busca por um sorriso estético, a procura por procedimentos menos invasivos, como a restauração em resina composta e o clareamento dental, também aumentou. As resinas compostas apresentam propriedades ópticas, sendo que uma destas propriedades é a fluorescência, que destina-se a dar naturalidade à restauração mimetizando-as à de
Publicado em: 2010
-
46. Mensuração da contração de polimerização de resinas compostas através da microscopia eletrônica de varredura = Mensuration of the polimerization shrinkage of composites through scanning electron microscope / Mensuration of the polimerization shrinkage of composites through scanning electron microscope
O presente estudo avaliou três diferentes marcas comerciais de compósitos quanto à fenda resultante da contração de polimerização: Esthet-X (Dentsply); Filtek Z350 (3MESPE); Concept (Vigodent) todos na cor A3. Os compósitos foram inseridos numa matriz metálica com 7mm de diâmetro interno e 2mm de altura, sendo prensados entre 2 placas de vidro e fo
Publicado em: 2010
-
47. Selamento de lesões cariosas oclusais : um ensaio clínico randomizado
As evidências mostram uma redução ou eliminação significativa na quantidade de bactérias viáveis sob selantes e restaurações e consequente diminuição na progressão da cárie quando as bactérias se encontram separadas do meio bucal. O objetivo deste ensaio clínico controlado randomizado foi avaliar a eficácia de duas estratégias de tratamentos
Publicado em: 2010
-
48. Efeito da ciclagem térmica e imersão em clorexidina nas propriedades físicas das resinas de bisacrilato de metila e metacrilato de metila / Effect of thermo cycling and chlorexidine immersion in physicals properties of bis-acryl and methacryl resins
O uso de resinas acrílicas para confecção de restaurações provisórias é bastante difundido na prática odontológica. Dois tipos de resina encontram-se comercialmente disponíveis, as de bisacrilato de metila e as de metacrilato de metila e, em decorrência das exigências funcionais e estéticas das restaurações provisórias, estes materiais devem
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 02/06/2009