1. Avaliação da utilização da pós cura nas propriedades térmicas e mecânicas de um sistema epóxi de cura à temperatura ambiente
RESUMO Neste trabalho, uma resina epóxi de cura a temperatura ambiente foi submetida a ciclos térmicos de pós cura para verificar as alterações nas propriedades térmicas e mecânicas finais do material. As amostras foram obtidas por vazamento em molde metálico e os ciclos de pós cura foram realizados a 75°C, 90°C, 110°C por uma hora e um ciclo de
Matéria (Rio J.). Publicado em: 16/09/2019
-
2. Cellulose Nanocrystals and Jute Fiber-reinforced Natural Rubber Composites: Cure Characteristics and Mechanical Properties
A comparative study was conducted for three natural rubber (NR) composites: one containing raw jute fibers, one containing bleached jute fibers, and one containing cellulose nanocrystals (CNCs). The composites were prepared by adding each filler at 5 or 10 phr to the latex before chemical coagulation, and the composites were processed in a two-roll mixing mi
Mat. Res.. Publicado em: 26/08/2019
-
3. Evaluation of Out-of-Autoclave (OOA) epoxy system
Abstract Epoxy resins (EP) usually cure in autoclave to minimize resin voids and to achieve the desired resin/fiber ratio. Cure parameters such as temperature, vacuum and pressure levels are controlled and monitored. Aiming time and cost optimization, new out-of-autoclave (OOA) cure processes have been developed lately. This study evaluated the cure cycle an
Polímeros. Publicado em: 2017-12
-
4. OPTIMIZATION OF A PULTRUSION PROCESS USING FINITE DIFFERENCE AND PARTICLE SWARM ALGORITHMS
AbstractPultrusion is one of several manufacturing processes for reinforced polymer composites. In this process fibers are continuously pulled through a resin bath and, after impregnation, the fiber-resin assembly is cured in a heated forming die. In order to obtain a polymeric composite with good properties (high and uniform degree of cure) and a process wi
Braz. J. Chem. Eng.. Publicado em: 2015-06
-
5. ESTUDO DE UM REATOR SOLAR HÍBRIDO PARA CURA ACELERADA DO CONCRETO EM ÁGUA MORNA. / STUDY OF A HYBRID SOLAR REACTOR FOR ACCELERATED CURING OF CONCRETE IN WARM WATER.
The Portland cement concrete material is the most consumed after the water worldwide due to their versatility molding, strength and durability as a structural material. The curing is the procedure that aims to keep the concrete saturated with water in their early ages and it is essential to ensure the reactions of cement hydration, promoting its consolidatio
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 01/11/2012
-
6. Imobilização da tanase de Paecilomyces variotii e ação em reações de hidrólise e síntese / Immobilization of tannase from Pecilomyces variotii and reactions of hydrolysis and synthesis
Tannin acyl hydrolase (TAH) known as tannase (EC 3.1.1.20) is an enzyme that hydrolyzes esters of hydrolysable tannins producing gallic acid and glucose as the reaction medium is polar. However, the literature indicates their ability to produce also gallic acid esters in organic media. Our research group has isolated a fungus, Paecilomyces variotii, tannase
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 06/06/2012
-
7. CFD-optimization algorithm to optimize the energy transport in pultruded polymer composites
Pultrusion is a composite manufacturing process in which fibers are pulled continuously through a resin bath for resin impregnation before entering into a heated die, where an exothermic cure reaction occurs. The energy needed to provide the cure reaction depends on many aspects such as cure kinetics and pulling speed. Generally, the pultrusion forming is di
Braz. J. Chem. Eng.. Publicado em: 2012-09
-
8. Effect of pre-heated dual-cured resin cements on the bond strength of indirect restorations to dentin
This study evaluated the effects of resin luting agents (LA) polymerized using increased temperature on the in vitro microtensile bond strength (mTBS) of indirect restorations to dentin. The occlusal dentin surfaces of 40 human third molars were exposed and flattened. The teeth were assigned to 8 groups (n = 5) according to the LA temperature (25°C o r 50°
Brazilian Oral Research. Publicado em: 2012-04
-
9. Pre-heated dual-cured resin cements: analysis of the degree of conversion and ultimate tensile strength
This study evaluated the degree of conversion (DC) and ultimate tensile strength (UTS) of dual-cured resin cements heated to 50º C prior to and during polymerization. Disc- and hourglass-shaped specimens of Rely X ARC (RX) and Variolink II (VII) were obtained using addition silicon molds. The products were manipulated at 25º C or 50º C and were subjected
Brazilian Oral Research. Publicado em: 2011-04
-
10. Estudio cinético del efecto de polifenilsulfona sobre el curado de una resina epoxi/amina mediante calorimetría diferencial de barrido convencional y modulada con temperatura: parte II
In this work we studied the effect of the addition of the linear thermoplastic polyphenyl sulfone (PPSU) on the cure kinetics and the thermal properties of a resin based on diglycidyl ether of bisphenol-A (DGEBA), cured with 4,4´-diaminodiphenyl sulfone (DDS). The kinetic study and the characterization process have been carried out by using differential sca
Polímeros. Publicado em: 12/11/2010
-
11. Diffusion of plasticizer in a solid propellant based on hydroxyl-terminated polybutadiene
The aim of this work was to determine the dioctyl azelate (DOZ) plasticizer diffusion coefficient (D) for samples containing the interfaces of rubber, liner and solid composite propellant based on hydroxyl-terminated polybutadiene (HTPB). The samples used in the diffusion study were aged up to 31 days after the cure period at 80 °C. A computer program imple
Polímeros. Publicado em: 12/11/2010
-
12. Efeito do protocolo de ativação da polimerização e envelhecimento acelerado em algumas propriedades de cimentos resinosos / Effects of polymerization activation protocol and accelerated aging in some resin cements properties
The study aimed to evaluate the effects of curing protocol and accelerated aging on some properties of dual-cure resin cements. Additionally, the effects of different ambient temperature and aging on the working and setting times were investigated when cements were self-cured only. Properties evaluated were degree of conversion as determined by FTIR-ATR spec
Publicado em: 2010