1. Metal-Supported Niobium Catalysts Investigation for Conversion of Bio-Renewable Glycerol to Organic Compounds
The glycerol oxidative dehydration to organic compounds, especially acrolein and acrylic acid, was studied over vanadium, molybdenum, and cobalt oxides supported on niobium oxide and niobium phosphate catalysts. At 300 °C, the glycerol conversion was 100% over all catalysts tested, and acrolein was the main product observed, without significant deactivation
Journal of the Brazilian Chemical Society. Publicado em: 2022
-
2. Catalytic Removal of Toluene from Air Streams by Cobalt Oxide Supported on Sepiolite
Removal of toluene using cobalt oxide supported on sepiolite catalysts was investigated. Deposition precipitation method was used to prepare the catalysts. The catalysts were characterized using X-ray diffraction, field emission scanning electron microscopy, energy dispersive X-ray spectroscopy, thermogravimetric analysis (TGA) and Brunauer-Emmet-Teller meth
J. Braz. Chem. Soc.. Publicado em: 16/09/2019
-
3. Carbon Nanotube-Supported Copper-Cobalt Catalyst for the Production of Higher Carbon Number Alcohols through Carbon Monoxide Hydrogenation
A series of carbon nanotube (CNTs)-supported copper-cobalt catalysts were prepared and investigated in a slurry reactor for their ability to selectively convert syngas into higher carbon number alcohols. The 7.5Cu7.5Co/CNTs catalyst achieved superior selectivity towards the formation of ethanol (30.1%) and C2+ alcohols (57.7%), while the 10Co5Cu/CNTs catalys
J. Braz. Chem. Soc.. Publicado em: 2018-07
-
4. Catalytic oxidation of volatile organic compounds (n-hexane, benzene, toluene, o-xylene) promoted by cobalt catalysts supported on γ-Al2O3-CeO2
Cobalt catalysts supported on γ-alumina, ceria and γ-alumina-ceria, with 10 or 20%wt of cobalt load, prepared by the wet impregnation method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), field emission transmission electron microscopy (FETEM), N2 adsorption-desorption isotherms (BET/BJH methods), energy-dispersive X-ray
Braz. J. Chem. Eng.. Publicado em: 2014-09
-
5. Conversão química de no e co sobre catalisadores à base de óxidos de cobalto ou de ferro
Cobalt or iron oxides supported or not on zeolite Hbeta were prepared and evaluated in the reduction reaction of NO by CO in presence of O2, SO2 or H2O. XRD results evidenced the Hbeta structure and the formation of Co3O4 and Fe2O3. TPR-H2 analysis showed complete reduction of cobalt oxide at lower temperatures than for iron oxide. The catalysts are quite ac
Quím. Nova. Publicado em: 2014-04
-
6. Study of cobalt catalysts supported on CeO2-La2O3-SiO2 for the production of hydrogen from steam reforming of ethanol / Estudo de catalisadores de cobalto suportados em matrizes de La2O3-CeO2-SiO2 para a produção de hidrogênio a partir da reforma a vapor do etanol
No presente trabalho, foram estudados catalisadores de Co10%SiO2, com adições de La2O3 e CeO2, para a reação de reforma a vapor do etanol (RVE), visando aumentar a atividade catalítica e reduzir a formação de carbono sobre o catalisador. O teor mássico de cobalto utilizado foi de 10%, enquanto que os teores de La e Ce seguiram as seguintes proporçõ
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 17/08/2012
-
7. Sobre a estabilidade de catalisadores de cobalto suportados durante a reforma do etanol
Catalisadores de cobalto suportados em γ-alumina e aluminato de magnésio modificados com lantânio e cério foram aplicados a diferentes condições de reforma do etanol. O desafio inicial foi tentar controlar a taxa de acúmulo de carbono, um dos principais fatores de desativação de catalisadores em condições de reforma a vapor do etanol. Análise
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 11/06/2012
-
8. Sintese de nanotubos de carbono por CVD utilizando catalisadores à base de ferro e molibdênio suportados em matrizes cerâmicas
Molybdenum is known for its synergistic effect in the synthesis of carbon nanotubes (CNs) by chemical vapor deposition (CVD method). When added to typical catalysts like iron, nickel, and cobalt, even in small quantities, it is increases the yield of these nanostructures. The presence of Mo also has an influence on the type and number of CN walls formed. Alt
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 26/02/2010
-
9. Preparação, caracterização e avaliação de óxidos de ferro e cobalto suportados em carvão ativado polimérico como catalisador na reação de desidrogenação do etilbenzeno / Preparation, characterization and evaluation of iron oxides and cobalt supported on activated carbon and polymeric catalysts for the dehydrogenation of ethylbenzene
Neste trabalho foram sintetizados catalisadores suportados em carvões ativados, que foram obtidos por meio da carbonização de uma matriz polimérica. O precursor do carvão ativado foi o copolímero de estireno e divinilbenzeno sulfonado, que foi sintetizado por meio de polimerização em suspensão, na presença de diluentes inertes para a produção de
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 09/02/2010
-
10. Preparation, characterization and evaluation of iron oxides and cobalt supported on activated carbon and polymeric catalysts for the dehydrogenation of ethylbenzene / Preparação, caracterização e avaliação de óxidos de ferro e cobalto suportados em carvão ativado polimérico como catalisador na reação de desidrogenação do etilbenzeno
In this work were synthesized catalysts supported on activated carbons, which were obtained by carbonization of a polymer matrix. The precursor of activated carbon was the sulfonated styrene-divinylbenzene copolymer, which was synthesized by suspension polymerization in the presence of inert diluents to produce a macroporous network structure. The chemical m
Publicado em: 2010
-
11. Enhancing cobalt dispersion in supported Fischer-Tropsch catalysts via controlled decomposition of cobalt precursors
Fischer-Tropsch synthesis is a part of Gas-to Liquids (GTL), Biomass-to-Liquids (BTL) and Coal to Liquids (CTL) technologies, which produce alternatives clean fuels from natural gas, biomass and coal. The catalytic performance of cobalt catalysts in Fischer-Tropsch synthesis strongly depends on the size of cobalt particles in nanoscale range (6-30 nm). Cobal
Brazilian Journal of Physics. Publicado em: 2009-04
-
12. Geração de H2 a partir do etanol : efeito da adição de terras raras (La2O3, CeO2) e Pt nas propriedades atalíticas de Co/Al2O3 para reforma do etanol
Ni or Co catalysts supported on Al2O3, La2O3-Al2O3 and CeO2-Al2O3 were prepared by impregnation of Al2O3 with an aqueous solution of lanthanum nitrate or ceria, followed by a calcination and incipient wetness impregnation with an aqueous solution of nickel or cobalt nitrate and promoted with Ag or Pt. The catalysts were characterized by temperature-programme
Publicado em: 2009