Synthesis, Characterization and Dry Sliding Wear Behavior of In-situ Formed TiAl3 Precipitate Reinforced A356 Alloy Produced by Mechanical Alloying Method
AUTOR(ES)
Dursun, Özyürek, Tansel, Tuncay, Hatice, Evlen, İbrahim, Çiftci
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
2015-08
RESUMO
In this present study, the effect of in-situ formed TiAl3 and AlTiSi intermetallic phases within A356 aluminum alloy on the dry sliding wear behaviors was investigated. The TiAl3 and AlTiSi intermetallic phases were obtained by synthesizing A356 aluminum alloy containing 6% titanium for different times (1, 4, 8 and 16h). The cold pressed samples were sintered in an argon atmosphere at 530 °C for one hour (10 °C/min.) and then cooled in the furnace. The sintered samples were synthesized at 550 °C for different times (1, 4, 8 and 16h), and the in-situ aluminum matrix composites (AMCs) were produced. Wear tests of the AMCs were performed under 30 N load and at 1 ms-1sliding speed for five different sliding distances. As the result of the studies performed, formation of in-situ TiAl3 and AlTiSi intermetallic phases were detected. With the increase in synthesizing time, the porosity in the structure was found to be reduced. In addition, it was observed that the densities and hardness of the composites increased depending on the synthesizing time. The wear test results revealed that increasing hardness values of A356 + 6% Ti AMCs decreased the weight loss.
Documentos Relacionados
- Electrochemical behavior of Ti/Al2O3 interfaces produced by diffusion bonding
- SÍNTESE POR REDUÇÃO IN-SITU E CARACTERIZAÇÃO MICROESTRUTURAL DOS NANO-COMPÓSITOS CU-AL2O3 E NI-AL2O3
- Effect of heat treatment on microstructures and mechanical properties in a full lamellar PM TiAl alloy
- Synthesis, Microstructural Characterization and Microhardness of AlCoNi-SiC Composite Prepared by Mechanical Alloying
- Preparação de materiais compositos in-situ a partir de ligas euteticas nos sistemas Nb-Al-Ti e Nb-Al-Cr