SYNTHESIS AND CHARACTERIZATION OF NANOSTRUCTURED IRON-NICKEL ALLOYS / SÍNTESE E CARACTERIZAÇÃO DE LIGAS FE-NI NANOESTRUTURADAS
AUTOR(ES)
ORFELINDA AVALO CORTEZ
DATA DE PUBLICAÇÃO
2008
RESUMO
Nickel oxide and hematite nanostructured were successfully prepared by thermal decomposition from nickel nitrate hexahydrate and ferric nitrate nonahydrate in the temperature range of 350-450°C with variation of the time. The average crystallite sizes of NiO and Fe2O3 were estimated from X-ray diffraction (XRD) peaks using the PowderCell and Topas software. We observed that the crystallite size changes as a function of synthesis temperature. The significant result was the large size of the resulting NiO crystallites, which increased from 31nm (T=350°C, 3hr) to 98nm (T=450°C, 5hr). Kinetic studies of the reduction of NiO and Fe2O3 by hydrogen in the temperature range 250-600°C have been investigated. Nanostructured Fe-Ni alloys with compositions FexNi100-x (x = 25, 50, and 75 w%) have been successively prepared by thermal decomposition from mixtures of nitrates (formation of oxides) and reduction by hydrogen at 700ºC (formation of alloys). The Fe-Ni alloys, characterized by X-ray diffraction show crystallites sizes about 25nm. The Nirich phase, Fe25Ni75 alloys show the existence of γ(FCC) phase. The Fe50Ni50 alloy show the existence of tetragonal phase. The Fe-rich phase, Fe75Ni25 alloy, contain a mixture of α(BCC) and γ(FCC) phases. The coexistence of these phases is attributed to phase segregation occurring in these alloys as a result of enhanced atomic diffusion. It was inferred from results of magnetic measurements at 300K, that nanostructured Fe-Ni alloys were in a superparamagnetic state.
ASSUNTO(S)
thermal decomposition ligas ferroniquel reduction by hydrogen decomposicao termica reducao por hidrogenio iron-nickel alloys
ACESSO AO ARTIGO
Documentos Relacionados
- Mechanical Behavior of Electrodeposited Bulk Nanocrystalline Fe-Ni Alloys
- Martensite Transformation Intergrain and Intragrain Autocatalysis in Fe-Ni alloys
- Synthesis, Characterization and Electromagnetic Properties of SnO-coated FeNi Alloy Nanocapsules
- THE INFLUENCE OF DIFFERENT ELECTROLYTES ON SULFENTRAZONE DECHLORINATION BY IRON-NICKEL BIMETALLIC NANOPARTICLES
- Produção e caracterização de uma liga Fe-Ni obtida por processamento coloidal aquoso e reação de estado sólido