Study of Cellulose Nanocrystals and Zinc Nitrate Hexahydrate Addition in Chitosan Hydrogels
AUTOR(ES)
Ferreira, Sheila de Oliveira
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
25/04/2019
RESUMO
In this study, chitosan hydrogels were produced with 0, 2, 4 and 6 wt% of cellulose nanocrystals (CNC) using hexahydrate zinc nitrate (Zn(NO3)2.6H2O) as a catalyst for chitosan crosslinking reaction. CNC´s size was estimated by dynamic light scattering (DLS) and surface charge by zeta potential. Hydrogels were characterized by rotational rheometer, swelling test, uniaxial compression test, in vitro degradation, scanning electron microscopy (SEM) and microtomography. Results showed that zinc nitrate and CNC addition did not influence mechanical properties, degradation, and morphology of the hydrogels. However, zinc nitrate decreased 36.54% of the gel time and 41.37% of the swelling degree, and increased the crosslinking degree of the chitosan hydrogels, proving not only its catalytic effect but also its participation in the crosslinking reaction. Porosity was slightly reduced after addition of zinc nitrate and incorporation of CNC. In the mechanism of crosslinking reaction, a competition between CNC and zinc nitrate was observed.
Documentos Relacionados
- Cellulose nanocrystals from coconut fiber: Preparation and Characterization.
- Biocompatibility of a New Dental Glass Ionomer Cement with Cellulose Microfibers and Cellulose Nanocrystals
- Mechanical, thermal, and barrier properties of methylcellulose/cellulose nanocrystals nanocomposites
- THE EFFECT OF CELLULOSE NANOCRYSTALS IN SUGARCANE BAGASSE PARTICLEBOARDS OF PITH AND FIBERS
- Nanocomposite Films Based on Flaxseed Gum and Cellulose Nanocrystals