Síntese do pigmento cerâmico verde vitória (Ca3Cr2Si3O12) a partir de CaCO3, Cr2O3 e SiO2
AUTOR(ES)
Della, Viviana Possamai, Junkes, Janaina Accordi, Rambo, Carlos Renato, Hotza, Dachamir
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2008
RESUMO
The synthesis of the ceramic pigment Victoria Green (Ca3Cr2Si3O12 ) is described. As raw materials CaCO3, Cr2O3, and SiO2 obtained from rice husk were used. Borax was used as mineralizer. Raw materials were formulated stoichiometrically and calcined from 1000 to 1200 ºC for 180 min. The main phase detected was uvarovite with particle size below 45 mm. The pigments were applied on ceramic tiles and sintered at 1150 ºC for 40 min. The synthesis process showed to be adequate to produce the green pigment, whose characteristics resemble those of a commercial pigment.
Documentos Relacionados
- Efeito de formulações de dentifricios com CaCO3 versus SiO2 na inibição da desmineralização do esmalte dental : estudo in situ
- Efeito do Cr2O3 na mulitização do gel difásico Al2O3-SiO2
- Nanopartículas de Co suportadas em SiO2 : síntese, caracterização e propriedades catalíticas para a reforma a vapor do etanol.
- Síntese e caracterização estrutural, morfológica e óptica de partículas de PbCrO4 e Pb2CrO5 e sua dispersão em SiO2
- Síntese e caracterização de nanocompósitos Ni: SiO2 processados na forma de filmes finos