Obtenção de titânio metálico com porosidade controlada por metalurgia do pó

AUTOR(ES)

Braga, Neila de Almeida, Ferreira, Neidenêi Gomes, Cairo, Carlos Alberto Alves

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2007-04

RESUMO

Titanium is an attractive material for structural and biomedical applications because of its excellent corrosion resistance, biocompatibility and high strength-to-weight ratio. The high reactivity of titanium in the liquid phase makes it difficult to produce it by fusion. Powder metallurgy has been shown to be an adequate technique to obtain titanium samples at low temperatures and solid-phase consolidation. The production of compacts with different porosities obtained by uniaxial pressing and vacuum sintering is briefly reviewed. Powder particle size control has been shown to be very important for porosity control. Sample characterization was made using scanning electron microscopy (SEM) images.

Documentos Relacionados

• Obtenção de revestimentos de nitreto de titânio por meio de deposição física de vapores em ligas de titânio obtidas por metalurgia do pó
• Avaliação da absorção de elementos intersticiais no processo de obtenção de ligas de titânio por metalurgia do pó
• Elaboração e caracterização de compósitos titânio/hidroxiapatita por metalurgia do pó para aplicações biomédicas
• Estudo comparativo de amostras de NiTi produzidas por metalurgia do pó
• Pérolas diamantadas obtidas por metalurgia do pó: nacionalização da tecnologia