Modificação de poli(fluoreto de vinilideno) induzida por radiação gama para aplicação como compósito ionomérico de metal-polímero / Poly(vinylidene fluoride) modification induced by gamma irradiation for application as ionic polymer-metal composite

AUTOR(ES)

Henrique Perez Ferreira

FONTE

IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia

DATA DE PUBLICAÇÃO

25/07/2011

RESUMO

Gamma-radiation-induced grafting of styrene into poly(vinylidene fluoride) (PVDF) films with 0.125 mm thickness at doses from 1 to 100 kGy in the presence of a styrene/N,N- dimethylformamide (DMF) solution (1:1, v/v) and styrene/toluene (1:1, v/v) at dose rate of 5 kGy h-1 was carried out by simultaneous method under nitrogen atmosphere at room temperature, using gamma rays from a Co-60. After grafting reactions, the polymer was then sulfonated in chlorosulfonic acid/1,2-dichloroethane (2 and 10%) for 3 hours. The films were characterized before and after modification by calculating the degree of grafting (DOG), infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and thermogravimetry (TG/DTG). DOG results show that grafting increases with dose, and varies enormously depending on the solvent used, with DOGs about 20 times greater in DMF than in toluene. It was possible to confirm the grafting of styrene by FT-IR due to the appearance of the new characteristic peaks and by the TG and DSC which exhibited changes in the thermal behavior of the grafted/sulfonated material. Sulfonated material was also characterized by ion exchange capacity (IEC) showed that both DOG and sulfonic acid concentration increase IEC values. Results showed that it is possible to obtain materials with ion exchange capacity of possible application as ionic polymer-metal composites.

ASSUNTO(S)

compósito ionomérico de metal-polímero enxertia estireno grafting induzida por radiação ionic polymer-metal composite poli (fluoreto de vinilideno) poly(vinylidene fluoride) pvdf pvdf radiation induced styrene

Documentos Relacionados

• Processamento, caracterização e determinação do perfil de polarização do Poli(fluoreto de vinilideno)
• Processamento e caracterização de mantas de nanofibras eletrofiadas e orientadas de Poli(fluoreto de vinilideno)
• Preparação e caracterização de membranas poliméricas de poli(fluoreto de vinilideno) para uso em nanofiltração
• Characterization of a microvalve using the piezoelectric polymer poly(viniyidene fluoride) (PVDF) integrated to a micronozzle end
• Preparação e caracterização de nanocompósitos de poli(fluoreto de vinilideno) com poss e nanotubos de carbono