Mechanical spectroscopy study of the Cu36Zr59Al5 and Cu54Zr40Al6 amorphous alloys

AUTOR(ES)

Marques, Paulo Wilmar Barbosa, Chaves, Javier Muñoz, Silva Jr., Paulo Sérgio da, Florêncio, Odila, Garcia, Maira Martins, Aliaga, Luis César Rodríguez, Botta, Walter José

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

23/10/2012

RESUMO

A mechanical spectroscopy study of Cu-Zr-Al bulk metallic glasses, was performed with two types of equipment: a Kê-type inverted torsion pendulum and an acoustic elastometer, working in the frequency ranges of Hz and kHz, respectively, with a heating rate of 1 K/min. The analysis of the anelastic relaxation shows similar spectra for both types of equipment resulting in internal friction patterns that vary with temperature and are not reproducible at each thermal cycle. The normalized of the square of the frequency changes from the first to later measurement cycles. These results indicate that the specimens of Cu-Zr-Al alloys were changing by mechanical relaxation, owing to the motion of atoms or clusters in the glassy state and possible "defects" produced during the processing of alloys.

Documentos Relacionados

• Consolidation of the Cu46Zr42Al7Y5 amorphous ribbons and powder alloy by hot extrusion
• Propriedades mecânicas das ligas Ti34Cu36Ni8Zr22 e (TiZr)80Co12Fe8
• Mechanical Spectroscopy of Ti-15Zr-based Alloys with Mo Addition
• An Experimental Study of the Solidification Thermal Parameters Influence upon Microstructure and Mechanical Properties of Al-Si-Cu Alloys
• Interconnection between microstructure and microhardness of directionally solidified binary Al-6wt.%Cu and multicomponent Al-6wt.%Cu-8wt.%Si alloys