Consolidation of the Cu46Zr42Al7Y5 amorphous ribbons and powder alloy by hot extrusion
AUTOR(ES)
Melle, Ana Karla, Peres, Mauricio Mhirdaui, Bolfarini, Claudemiro, Botta, Walter José, Jorge Junior, Alberto Moreira, Kiminami, Claudio Shyinti
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
09/08/2012
RESUMO
The amorphous Cu46Zr42Al7Y5 alloy presents large supercooled liquid region (ΔT X = 100 K), with a viscosity of about 10(6) N.s/m² where the material can flow as a liquid, making it possible an easy deformation in this temperature region. The aim of this work was to analyze processing routes to produce bulks of metallic glasses. Two kinds of materials were used: amorphous powders and ribbons, both were consolidated by hot extrusion in temperatures inside the range between Tg and Tx, with a ram speed of 1 mm/min and extrusion ratio of 3 : 1. Analysis of X-Ray Diffratometry (XRD), Differential Scanning Calorimetry (DSC) and Scanning Electron Microscopy (SEM), revealed that the proposed consolidation routes were effective to produce large bulks of amorphous materials, even with the strong decreasing of ΔT X observed after deformation by milling and during extrusion.
Documentos Relacionados
- Hot Consolidation of Partially Amorphous Cu-Ti Based Alloy: a Comparison Between Hot Extrusion and Hot Compaction by Sintering
- Mechanical spectroscopy study of the Cu36Zr59Al5 and Cu54Zr40Al6 amorphous alloys
- Stability of an amorphous alloy of the Mm-Al-Ni-Cu system
- Study of Glass Forming on Cu60.0Zr32.5Ti7.5 Alloy by Molecular Dynamics Simulation
- Effect of Sn Addition in the Microstructure Refinement and Corrosion Resistance of Cu-Zr-Al-Ag Alloy