Investigação da estabilidade térmica e das propriedades elétricas do TiO2 em função da dopagem com Ce(SO4)2
AUTOR(ES)
Ana Carolina Paiva Carmo
DATA DE PUBLICAÇÃO
2008
RESUMO
The metalic oxides have been studies due to differents applications as materials semiconductor in solar cells, catalysts, full cells and, resistors. Titanium dioxide (TiO2) has a high electric conductivity due to oxygen vacancies. The Ce(SO4)2.2H2O doped samples TiO2 and TiO2 pure was obtained sol-gel process, and characterized by X-ray diffractometry,thermal analysis, and impedance spectroscopy. The X-ray diffraction patterns for TiO2 pure samples shows at 700C anatase phase is absent, and only the diffraction peaks of rutile phase are observed. However, the cerium doped samples only at 900C rutile in the phase present with peaks of cerium dioxide (CeO2). The thermal analysis of the TiO2 pure and small concentration cerium doped samples show two steps weight loss corresponding to water of hydration and chemisorbed. To larger concentration cerium doped samples were observed two steps weight loss in the transformation of the doped cerium possible intermediate species and SO3. Finally, two steps weight loss the end products CeO2 and SO3 are formed. Analyse electric properties at different temperatures and concentration cerium doped samples have been investigated by impedance spectroscopy. It was observed that titanium, can be substituted by cerium, changing its electric properties, and increased thermal stability of TiO2 anatase structure
ASSUNTO(S)
drx titanium tg/dta quimica tg/dta impedance impedância Óxido de cério drx cerium oxide titânio
Documentos Relacionados
- Copper and cobalt catalysts supported on CeO2, TiO2 and CeO2-TiO2 to reduction NO by CO
- Propriedades das argamassas de revestimento contendo resíduo proveniente da produção do TiO2 (MNR)
- TiO2 e TiO2 dopado com ferro : efeitos da inserção do dopante e da segregação de hematita nas propriedades e na atividade fotocatalítica para conversão de energia solar
- Estudo das propriedades acusticas do filme finode TiO2 usando SAW
- Influência do tipo precursor nas propriedades estruturais, morfológicas, dielétricas e magnéticas das nanopartículas de TiO2