Influencia de la adición de CuO sobre las propiedades dieléctricas y piezoeléctricas de cerámicos K1/2Na1/2NbO3
AUTOR(ES)
Ramajo, Leandro A., Taub, Jonathan, Castro, Miriam S.
FONTE
Matéria (Rio J.)
DATA DE PUBLICAÇÃO
2013-12
RESUMO
In this paper the influence of Cu on dielectric and piezoelectric properties of K1/2Na1/2NbO3 (KNN) was evaluated. Samples were obtained by solid state reaction doping with CuO (0 to 2 mol%). The obtained samples were characterized by the Archimedes method, X-Ray diffraction, Raman spectroscopy, Scanning Electron Microscopy, polarization curves, piezoelectric constant (d33) and impedance spectroscopy at room temperature. In general, it was observed that doping does not improve dielectric and piezoelectric properties. Small amounts of CuO (0.5 mol%) slightly affected the densification process, while high concentrations increased the porosity of the samples. Also, low concentrations of CuO drastically reduced d33 values, presumably due to the hardening effect of the additive.
Documentos Relacionados
- Modificación de las propiedades estructurales, eléctricas y magnéticas del BiFeO3 por la incorporación de Ba y Nb
- Efecto de la adición de bentonita sobre las propiedades ópticas de diferentes materiales compuestos poliméricos
- Análises térmicas e processo de sinterização da cerâmica KSr2Nb5O15 dopada com CuO
- Oxidação de propeno em catalisadores de CuO suportados em CeO2/y-alumina/cordierita
- Estrategias para obtenção de precursores unicos para a deposição de Nb2O5 ZrO2 e CuO por deposição quimica de vapor por metalorganicos