Influência da quantidade de amônio na síntese de nanopartículas de óxido de ferro por microemulsão
AUTOR(ES)
Fernandes, Maria Tereza Cortez, Kawachi, Elizabete Yoshie
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2010
RESUMO
Iron oxide nanoparticles were synthesized in microemulsion systems composed by Triton X-100/hexyl alcohol/cyclohexane/aqueous solution. The nanoparticles were synthesized in microemulsions containing different amounts of ammonium, in order to evaluate the influence of this parameter on the size of the nanoparticles and on the phase transformation after heat treatment. Powder materials were obtained after centrifugation, washing and drying, and they were analyzed as synthesized and after heating at 350, 500 and 1000 °C. It was observed that the higher amount of ammonium induced smaller particles and minor phase transformation, possibly due to a preferential nucleation process.
Documentos Relacionados
- Síntese de nanopartículas de óxido de ferro por microemulsão: influência do pH e do encapsulamento por sílica.
- Síntese e caracterização de nanopartículas de óxido de ferro e de grafite magnética fluida (GMF)
- Estudo do efeito da quantidade de óxido de ferro em cinzas pesadas de carvão mineral na obtenção de vitrocerâmicos
- Síntese e caracterização de nanopartículas de óxido de ferro suportadas em matriz carbonácea: remoção do corante orgânico azul de metileno em água
- Monitoramento in vivo por imagem por ressonância magnética de células C6 de glioma marcadas com nanopartículas superparamagnéticas de óxido de ferro