Influência da ciclagem térmica e mecânica em água na resistência ao cisalhamento da união infraestrutura/porcelana de cobertura de diferentes sistemas totalmente cerâmicos / Shear bond strength of all-ceramics core/veneer interface and its susceptibility to thermal and mechanical cycling

AUTOR(ES)

Hugo Alberto Vidotti

FONTE

IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia

DATA DE PUBLICAÇÃO

23/05/2011

RESUMO

The objective of this study was to evaluate the influence of thermal and mechanical cycling on the shear bond strength of different all-ceramic cores and veneering porcelain interfaces. It was also to characterize chemically the interfaces by energy dispersive spectroscopy (EDS). The allceramic systems tested were lithium dissilicate (DL), zirconia veneered by layering technic (ZC) or pressing technic (ZI) and glass infiltrated alumina (AI). A CoCr group was used as control. Twenty cylindrical specimens for each system were subjected to shear bond strength in a universal testing machine with a 0.5 mm/min crosshead speed. Half of the specimens (n=10) were thermal and mechanical cycled before shear bond strength was carried out. Mean shear bond strength (MPa) were analyzed with a 2-way analysis of variance and the Tukey test. Failures were classified with tereomicroscope and scanning electron microscope (SEM) analysis. In an addition, energy dispersive X-ray spectroscopy (EDS) analysis was performed from core/veneer interfaces. Thermal and mechanical cycling did not influence statistically on the shear bond strength for the systems evaluated. However, there was a statically significant difference between the systems evaluated. Control group (CoCr) presented the highest values (34,72 ± 7,05 Mpa), followed by DL (27,07 ± 5,28), ZI (23,58 ± 2,71), ZC (22,46 ± 2,08) e AI (18,15 ± 1,99). Thermal and mechanical cycling did not influence statistically on the shear bond strength for the systems evaluated. Failure modes were predominantly adhesive for CoCr group, cohesive in the core for DL, cohesive in veneer for groups ZC and ZI and mixed for AI. EDS analysis showed a interaction zone for all systems evaluated. Thus, it is possible to suggest, trough EDS analysis, that there is a chemical bond between core and veneer materials and that the shear bond strength variations can be related to intrinsic factors within veneering porcelain or to its wetting capacity.

ASSUNTO(S)

cerâmica ceramics interface interface porcelain porcelana

Documentos Relacionados

• Resistência de união da interface coping cerâmico pilar de implante variando o agente cimentante antes e após ciclagem térmica
• "Influência do volume de adesivo e das ciclagens térmica e mecânica na resistência de união resina-dentina"
• Influence of the concentration of hydrofluoric acid and thermal cycling on bond strength between ceramic and resin cement
• Efeito do envelhecimento por ciclagem mecânica ou ciclagem em autoclave na resistência à flexão de cerâmicas odontológicas
• AVALIAÇÃO DA INFLUÊNCIA DA CICLAGEM TÉRMICA E MECÂNICA NA EFETIVIDADE DA INTERFACE ADESIVA