Influence of sintering parameters on the microstructure and mechanical properties of nanosized 3Y-TZP ceramics

AUTOR(ES)

Palmeira, A. A.; Cangani, M. P.; Rodrigues Jr, D.; Strecker, K.; Santos, C. dos

FONTE

Cerâmica

DATA DE PUBLICAÇÃO

2021-03

RESUMO

Abstract The fracture toughness of 3Y-TZP ceramics obtained from a nanocrystalline powder with an optimized microstructure and highly transformable tetragonal grains was investigated. Samples of ZrO2-3 mol% Y2O3 were sintered at temperatures between 1250 and 1400 °C, with isothermal holding times of up to 16 h. Samples sintered at 1250 °C exhibited relative densities ranging between 92% and 98%, which increased with increasing isothermal duration, while samples sintered at 1300, 1350, or 1400 °C achieved densification higher than 98% for all isothermal treatments. Crystallographic analysis indicated the presence of a highly transformable ZrO2-tetragonal phase ( c / a √ 2 = 1 . 0148 - 1 . 0154 ) for all conditions studied. The average grain size ranged from 0.18±0.04 mm (1250 °C-0 h) to 0.64±0.08 mm (1400 °C-16 h), indicating activation energy of 141.3 kJ/mol for grain growth and a growth exponent of 2.8. Both Vickers hardness (1025 to 1300 HV) and fracture toughness (4.0 to 7.8 MPa.m1/2) increased with increasing sintering temperature and time due to increased densification, reduced porosity, and maintenance of potentially high fracture toughness by the t→m phase transformation.

Documentos Relacionados

• Effects of argon plasma and aging on the mechanical properties and phase transformation of 3Y-TZP zirconia
• Performance of 3Y-TZP bioceramics under cyclic fatigue loading
• Strength of 3Y-TZP and feldspathic porcelain subjected to different cooling methods
• Low-Fusing Porcelain Glaze Application on 3Y-TZP Surfaces can Enhance Zirconia-Porcelain Adhesion
• Deposition of SiOx thin films on Y-TZP by reactive magnetron sputtering: influence of plasma parameters on the adhesion properties between Y-TZP and resin cement for application in dental prosthesis