Hot Consolidation of Partially Amorphous Cu-Ti Based Alloy: a Comparison Between Hot Extrusion and Hot Compaction by Sintering

AUTOR(ES)
FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

2015-06

RESUMO

Consolidation of amorphous powders, which take advantage of the supercooled liquid region, is an alternative way to overcome the size limitation in marginal metallic glasses. Cu36Ti34Zr22Ni8based amorphous powders were obtained during high energy ball-milling. The analyses revealed that amorphous structures of powders and ribbons are quite different and this led to a different thermal behavior being the powders more thermally stable than the ribbons. Extrusion was initially proposed as a consolidation process; however, the decrease in viscosity in remainder amorphous matrix was not sufficient for that process, but certainly sufficient for sintering the sample during hot consolidation. An amorphous/nanocrystalline microstructure known for enhancing the mechanical properties of their fully amorphous counterparts was obtained. Evaluation of mechanical properties by microhardness revealed the relatively high hardness of HV 768. From these results, consolidation by sintering seems a promising route to produce bulk metallic glasses nanocomposites.

Documentos Relacionados