Estudo da oxidação superficial de ligas odontológicas de Ni-Cr em plasma pulsado para uso em restaurações metalocerâmicas
AUTOR(ES)
Tatiana Oliveira de Souza
DATA DE PUBLICAÇÃO
2008
RESUMO
Metal ceramic restorations matches aesthetic and strength, and in your making occurs an interface oxide layer, wetting resulting and atomic and ionic interactions resulting between metal, oxide and porcelain. However, frequent clinical fails occurs in this restoration type, because lost homogeneous deposition oxide layer and lost interface bond. Thus, in this study, thought depositate homogeneous oxide films above Ni-Cr samples surfaces polite previously, at plasma oxide environment. Six samples was oxided at 300 and 400C at one hour, and two samples was oxided in a comum chamber at 900C, and then were characterized: optical microscopic, electronic microscopic, micro hardness, and X ray difratometry. Colors stripes were observed at six samples plasma oxided and a grey surface those comum oxided, thus like: hardness increase, and several oxides from basic metals (Ni-Cr)
ASSUNTO(S)
plasma engenharia mecanica restaurações metalocerâmicas plasma pulsado ni-cr metal ceramic restorations oxidação oxidation ni-cr
Documentos Relacionados
- Microdureza de ligas de Ni-Cr fundidas sob diferentes condições
- Ataque quimico para promover microrretenções na superficie de ligas metalicas dos sistemas Ni-Cr e Ni-Cr-Be
- Efeito de diferentes tipos de soldagem na resistência à tração de estruturas fundidas com ligas de Ni-Cr
- Estudo eletroquímico de ligas à base de cobalto-cromo e níquel-cromo
- Microstructural evidence of beryllium in commercial dental Ni-Cr alloys