Emprego de óxidos tipo perovskita nas oxidações do propano e CO

AUTOR(ES)

Silva, Paulo Roberto Nagipe da

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2004-02

RESUMO

Simultaneous oxidation/co-precipitation of an equimolar mixture of La(III) and Co(II) nitrates and La(III) nitrate and Mn(II) chloride afforded a hydroxide gel, which was converted to LaCoO3 and LaMnO3 on calcination at 600 °C. After calcination, the obtained perovskites have been characterised by X-ray diffraction (XRD), X- ray photoelectron spectroscopy (XPS), thermogravimetric analysis (DTA - TGA) and BET specific surface determination. Specific surface areas of perovskites were 12 - 60 m²/g. XRD analysis showed that LaCoO3 and LaMnO3 are simple phase perovskite - type oxides. Traces of LaOCl, in addition to the perovskite were detected in the LaMnO3. The catalytic behavior was examined in the propane and CO oxidation. The LaCoO3 catalyst was more active to CO2 than the LaMnO3 catalyst.

Documentos Relacionados

• Óxidos do tipo perovskita para reação de redução de no com CO
• Estudo da oxidação total do etanol usando óxidos tipo perovskita LaBO3 (B= Mn, Ni, Fe)
• Preparação e aplicação de óxidos tipo perovskita La1-xCexNiO3 e La1-xCaxNiO3 para obtenção de gás de síntese a partir do metano.
• Caracterização estrutural e elétrica de óxidos semicondutores do tipo espinélio.
• Catalisadores de níquel e cobalto obtidos a partir de óxidos do tipo perovskita para reações de reforma a vapor de etanol