Óxidos do tipo perovskita para reação de redução de no com CO
AUTOR(ES)
Tanabe, Eurico Y., Assaf, Elisabete M.
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2009
RESUMO
In this work, the perovskite-type oxides LaNiO3, LaMnO3, La0,7Sr0,3NiO3 and La0,7Sr0,3MnO3 were prepared by co-precipitation and tested in the NO reduction with CO at 400 and 500 ºC for 10 h. The catalysts were characterized by X-ray diffraction, temperature programmed reduction with hydrogen, nitrogen adsorption and chemical analysis. The nonstoichiometric oxygen was quantified by temperature programmed reduction, and the catalytic tests showed that the La0,7Sr0,3MnO3 catalyst presented the higher performance for the reduction reaction of NO with CO. The partial substitution of lanthanum by strontium increased the NO conversion and the N2 yield.
Documentos Relacionados
- Emprego de óxidos tipo perovskita nas oxidações do propano e CO
- "Óxidos do tipo Perovskitas para reações de decomposição direta de NO e redução de NO com CO"
- Estudo da oxidação total do etanol usando óxidos tipo perovskita LaBO3 (B= Mn, Ni, Fe)
- Perovskitas preparadas pelo método do citrato como catalisadores para a reação de redução de NO com CO
- Reaproveitamento de óxidos de manganês de pilhas descartadas para eletrocatálise da reação de redução de oxigênio em meio básico