Embrittlement and Corrosion Decay of a Cast Duplex Stainless Steel
AUTOR(ES)
Matias, João Vitor Silva, Tavares, Sérgio Souto Maior, Pardal, Juan Manuel, Ribeiro, Ruan Stevan de Almeida
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
20/07/2017
RESUMO
Duplex stainless steels (DSS) are Fe-Cr-Ni-Mo alloys, with low carbon content, which have a favorable combination of mechanical properties and corrosion resistance. These characteristics are mainly attributed to a dual phase and refined microstructure, typical of these alloys, consisting of similar amounts of ferrite and austenite. For this reason, DSS are widely used in various segments of industry, especially in offshore applications. However, DSS components may have a decrease of their properties when they are exposed high temperatures, often due to incorrect manufacturing processes. Intermetallic phases may precipitate causing embrittlement and corrosion resistance decrease. This work presents the effects of short time aging at 475 °C on the mechanical properties and localized corrosion resistance of a cast DSS. The results show that mechanical properties, such as toughness and hardness, are more susceptible to aging, having already been affected during the first 4 hours of heat treatment, while the corrosion was affected in 12 h of aging.
Documentos Relacionados
- 475 °C Embrittlement in a duplex stainless steel UNS S31803
- Effect of Cooling Rate on the Corrosion Behavior of As-Cast SAF 2205 Duplex Stainless Steel After Solution Annealing Treatment
- Wear and Corrosion Study of Plasma Nitriding F53 Super duplex Stainless Steel
- Effect of thermal aging conditions on the corrosion properties and hardness of a duplex stainless steel
- Corrosion Resistance of Cu-Alloyed Precipitation Hardenable Duplex Stainless Steel ASTM A890 Grade 1B