Corrosion Resistance of Cu-Alloyed Precipitation Hardenable Duplex Stainless Steel ASTM A890 Grade 1B

AUTOR(ES)
FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

07/11/2019

RESUMO

Duplex stainless steels (DSS) are corrosion resistant alloys largely used in chemical and petrochemical industries. Some commercial DSS contain 0.5-1.0% copper addition to improve the corrosion resistance by reducing the corrosion rate in non-oxidizing environments. Higher copper addition (≥ 2%) can also hard by precipitation, especially when fine copper precipitates (ε phase) are produced. In this work, a cast copper alloyed DSS type ASTM A890 grade 1B with 3.01%Cu was investigated. Different levels of hardness were produced by solution treatment and aging at 450, 500, 550 and 600 oC for periods of time up to 1 hour. The corrosion resistance of aged DSS was evaluated by electrochemical tests in three media: 0.6 mol/L NaCl, 0.3 mol/L H2SO4 and 0.6 mol/L NaCl + 0.3 mol/L H2SO4 solutions. The results indicate that the effect of Cu addition depends on the media studied. Polarization studies in 0.6 mol/L NaCl showed a small anodic current peak occurred at around 400 mV vs. Ag/AgCl, with a strong influence on the passive film stability. Additionally, chronoamperometric measurements at 400 mV vs. Ag/AgCl showed a high electrochemical activity for the samples in 0.6 mol/L NaCl.

Documentos Relacionados