Corrosion of ASTM A 285 grade C steel welds used in celullose production by kraft process / Corrosão nas soldas do aço ASTM A 285 grau C empregados na obtenção de celulose pelo método Kraft
AUTOR(ES)
Valéria Motoyama
DATA DE PUBLICAÇÃO
2007
RESUMO
In this work samples of ASTM A 285 Grade C class steel, welded with covered electrodes AWS E7018 and AWS E6013, and with variations in the welding energy, were tested electrochemically, immersed in alkaline liquor, which is used in Kraft batch digesters. Workpieces were cut by electroerosion process from base metal (MB), heat affected zone (ZTA) and weld metal (MS), and submitted to metallographic characterization. A perlitic and ferritic microstructure was observed, with acicular ferrite surrounded by grain boundary ferrite and formation of Widmanstätten ferrite. Samples welded with AWS E7018 electrodes show microhardness profiles higher than AWS E6013 electrodes due to higher contents of manganese and silicon. Corrosion rates of MB, ZTA and MS regions increase with liquor temperature, and MS regions show corrosion rates higher than ZTA and MB, without heat treatment, for both electrodes. Values calculated were 0,30 mm/year for MB, 1,49 mm/year for ZTA and 2,63 mm/ano for MS with AWS E7018 electrode, without heat treatment, high energy, and for AWS E6013 electrode, in the same conditions, 1,24 mm/year for ZTA and 1,65 mm/year for weld metal.
ASSUNTO(S)
engenharia de materiais e metalurgica processo kraft aço 285 c covered electrodes eletrodos revestidos corrosion welding corrosão 285 c steel soldagem kraft process
ACESSO AO ARTIGO
http://www.bicen-tede.uepg.br/tde_busca/arquivo.php?codArquivo=171Documentos Relacionados
- Microstructural-mechanical characterization and corrosion resistance of the ASTM A890/ A890M 6A grade super duplex stainless steel
- Corrosion Resistance of Cu-Alloyed Precipitation Hardenable Duplex Stainless Steel ASTM A890 Grade 1B
- Análise da resistência à corrosão e ao desgaste do aço inoxidável austenítico ASTM F 138 tratado por laser
- Erosão, corrosão, erosão-corrosão e cavitação do aço ABNT 8550 nitretado a plasma
- Avaliação da resistência à corrosão em aços inoxidáveis ASTM F138 empregados em implantes ortopédicos