Avaliação da resistência à corrosão de implantes em aços inoxidáveis ISO 5832-9 e F138 removidos de pacientes
AUTOR(ES)
Silva, Elison da Fonseca e, Oliveira, Luiz Fernando Cappa de
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2012
RESUMO
This work has compared the surfaces of two different steel samples used as orthopedical implants, classified as ASTM F138 and ISO5832-9, through optical emission spectroscopy, by means of SEM and EDS. The samples (implants) were also submitted to potentiodynamic cyclic polarization in Ringer lactate and NaCl 0.9 M L-1 solutions; ISO5832-9 sample did not show any kind of localized corrosion, but in the case of F138 steel was observed a pit localized corrosion in both solutions. In Ringer lactate solution it was observed a loss of about 63% for nickel and 26% for iron for F138 stell, compared to the initial composition.
Documentos Relacionados
- Avaliação da resistência à corrosão em aços inoxidáveis ASTM F138 empregados em implantes ortopédicos
- Influencia da microestrutura sobre as propriedades mecanicas e resistencia a corrosão de um aço inoxidavel ISO 5832-9 - utilizado na fabricação de implantes ortopedicos
- STUDY OF THE DYNAMIC RECRYSTALLIZATION DURING THE DEFORMATION THE HOT ONE OF A STEEL ISO 5832-9
- Estudo eletroquímico comparativo do aço ISO 5832-9 em diferentes meios de interesse biológico
- Influencia do envelhecimento na microestrutura e propriedades mecanicas do aço inoxidavel ISO 5832-9