Análise por impedância eletroquímica \"on-line\" de conjuntos eletrodo/membrana (MEA) de células a combustível a membrana polimérica (PEMFC) / Analysis for impedance electrochemistry \"on-line\" of membrane/electrode assemble (MEA) of protons exchange membrane fuel cells (PEMFC)

AUTOR(ES)
FONTE

IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia

DATA DE PUBLICAÇÃO

15/08/2007

RESUMO

This work reports results of studies and characterization on Membrane Electrode Assemblies (MEAs) for Proton Exchange Membrane Fuel Cell (PEMFC). Some cell operation conditions and different processes of MEA production were investigated. The Electrochemical Impedance Spectroscopy Technique (EIS) (in situ - 0 to 16 A) was used \"on-line\" as a tool for diagnosis, concerning the cell performance. The EIS measurements were carried out with a FC350 Fuel Cell EIS System (GAMRY), coupled to a PC4 Potentiostat/Galvanostat and connected to the electronic load (TDI) for \"on-line\" EIS experiments (100 mHz - 10 kHz, dU = 5 mV). MEAs with 25 cm2 surface area, using PtM/C 20% (M = Ru, Sn or Ni) electrocatalysts were manufactured using the Alcohol Reduction Process (ARP). The catalytic ink was applied directly into the Carbon Cloth (GDL) and pressed in the NafionR membrane (105). MEAs using Pt/C and PtRu/C 20% from E-TEK electrocatalysts were manufactured by comparison. All the cathodes were sprayed with Pt/C 20% from E-TEK. The noble metal concentrations used were set to 0.4 mg Pt.cm-2 at the anode and 0.6 mg Pt.cm-2 at the cathode (E-TEK). Nyquist diagrams of the MEAs with Pt/C and PtRu/C from E-TEK or PtM/C (M = Ru, Sn or Ni) ARP showed essentially the same ohmic resistances for the MEAs. This fact can be explained by suppression of agglomerates during the MEA preparation process or by the homogeneity of the anchored electrocatalysts at the carbon surface. It could also be observed, at low current densities, that there was a significant performance difference between the electrocatalysts from E-TEK and those prepared with the Alcohol Reduction Process. The polarization curves results confirmed that the PtM/C (M = Ru, Sn or Ni) ARP showed an activity increase for the methanol and ethanol fed cells. The technique of EIE was shown efficient for the evaluation of the method preparation of MEAs and the acting of the cell, the results of EIE showed coherence in the choice of the model the electric circuit for MEAs using hydrogen, methanol and ethanol. This coherence indicates that other resistances no considered in the model are not relevant in the total resistance of MEAs.

ASSUNTO(S)

appropriate technology células a combustível electrocatalysts. electrochemistry impedance impedância eletroquímica met mev nanocatalisadores nanostructures nanotecnologia proton exchange membrane fuel cells spectroscopy xps

ACESSO AO ARTIGO

Documentos Relacionados