1. Characterization of Different Surface Layers Produced by Solid Boron-Nitro-Carburizing Thermochemical Treatment on AISI 1020
The aim of this study is to obtain and characterize surface layers on low carbon steel with the pack boron-nitro-carburizing process. Different mixtures of commercial powders (Turbonit® and Ekabor®) were used to investigate the case properties, microstructure and phases formation on AISI 1020 steel. A series of experiments were conducted in solid medium wi
Mat. Res.. Publicado em: 04/11/2019
-
2. Nitretação por descargas elétricas da liga Ti-6Al-4V com adição de pó abrasivo SiC ao fluido dielétrico
RESUMO O processo de nitretação que usa Usinagem por Descargas Elétricas é um método que associa a capacidade de usinar superfícies complexas com a obtenção de tratamento termoquímico de nitretação. A fonte de nitrogênio é proveniente da uréia, que compõe o fluido dielétrico juntamente com água deionizada. A liga de titânio Ti-6Al-4V possui
Matéria (Rio J.). Publicado em: 16/09/2019
-
3. Effects of Gas Nitriding on Fatigue and Crack Initiation of Ti6Al4V produced by Selective Laser Melting
Selective laser melting (SLM) is an additive manufacturing technique which permits fabrication of three dimensional parts by selectively melting consecutive layers of metallic powder. This allows the production of parts with high geometrical complexity. Titanium alloy Ti-6Al-4V (Ti64) is widely used in industry due to its high strength-to-mass ratio, corrosi
Mat. Res.. Publicado em: 15/07/2019
-
4. Morphology of the DIN 100Cr6 Case Hardened Steel after Plasma Nitrocarburizing Process
Nitrocarburizing is considered one of the most important thermochemical treatments for surface modification of metallic materials and involves the simultaneous diffusion of nitrogen and carbon onto the surface. Understanding and controlling the formation of the nitrocarburized layer have considerable industrial interest due to the improvements regarding wear
Mat. Res.. Publicado em: 04/04/2019
-
5. Wear resistance of AISI 304 stainless steel submitted to low temperature plasma carburizing
Abstract Despite the AISI 304 stainless steel has high corrosion/oxidation resistance, its tribological properties are poor, being one of the barriers for use in severe wear applications. Thus, there is a wide field for studying technologies that aim to increase the surface hardness and wear resistance of this material. In this work, hardness and wear resist
REM, Int. Eng. J.. Publicado em: 2017-09
-
6. Ionic Oxidation in Cathodic Cage of Titanium CP Grade II
Titanium oxides such as rutile and anatase, are materials that stand out for exhibiting properties that act in biomedical and photocatalytic applications, among others. It is extreme importance to idealize new techniques that produce such compounds, being indispensable the improvement of characterizations for these materials. For this purpose, titanium comer
Mat. Res.. Publicado em: 24/08/2017
-
7. Wear and Corrosion Study of Plasma Nitriding F53 Super duplex Stainless Steel
Super duplex stainless steels (SDSS) have high corrosion resistance because of their high contents of chromium, nickel, molybdenum and nitrogen but low wear resistance. To improve the wear resistance of these steels without affecting their corrosion resistance, samples of SDSS were treated by plasma ion nitriding at temperatures ranging from 350 °C to 570 �
Mat. Res.. Publicado em: 22/09/2016
-
8. AISI 1005 Steel Plasma Treated by Different Thermochemical Surface Treatments
Abstract To modify the surface structure of AISI 1005 steel and its properties without any dimensional loss, different plasma surface treatments were performed at low temperatures (500 ºC) in this study. The samples were subjected to single plasma treatments including: nitriding (N5% and N3%), carburizing (CE) and ferritic nitrocarburizing (NC) and to duple
Mat. Res.. Publicado em: 01/08/2016
-
9. Micro Abrasive Wear Behaviour Study of Carburization and Ion Plasma Nitriding of P20 Steel
P20 steel, which is mainly used in plastic molds, was thermochemically treated by ion plasma nitriding and solid and gas carburization. In this work, the solid and gas carburization were performed at 925 ºC for four different durations. The ion plasma nitriding was performed at 520 ºC for four different durations. The thermochemical treatment increased the
Mat. Res.. Publicado em: 29/04/2016
-
10. Study of the nitrided layer obtained by different nitriding methods
In this study, plasma nitriding, gas nitriding and solid nitriding were performed in AISI H13, AISI P20 and N-8550 tool steels. The aim of the study was compare the acquired properties after the thermochemical treatments and evaluate the efficiency of the solid nitriding treatment. The samples were analyzed using a microhardness tester and a scanning electro
Matéria (Rio J.). Publicado em: 2015-06
-
11. Efeito da ativação mecânica de uma formulação de talco/caulim/alumina sobre o mecanismo e a cinética de formação de cordierita
In this study, the influence of mechanical activation by intensive ball milling of a stoichiometric mixture of talc, kaolin, and alumina on the mechanism and kinetics of cordierite (2MgO·2Al2O3·5SiO2) formation was evaluated. The raw materials were characterized by chemical analysis, X-ray diffraction (XRD), laser diffraction, and helium pycnometry. The ki
Quím. Nova. Publicado em: 2014-04
-
12. Estudo do comportamento tribológico do aço AISI H13 submetido a tratamento termoquímico de boretação / Study of tribological behavior of AISI H13 steel subjected to boriding thermochemical treatment
In this work, solid boriding thermochemical treatment was carried out using Ekabor 1-V2 and one blend as boriding agents and heat treatment of quenching and tempering of AISI H13 tool steel in order to compare and evaluate the tribological behavior and the properties acquired for four studied conditions, that were: Ekabor powder boriding, Ekabor powder borid
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 18/06/2012